研究了在不同气氛下进行离子渗氮对TC 4钛合金渗氮层的组织与性能的影响。
The effect of the atmosphere on the structure and properties of ion nitriding layer of alloy TC4 was investigated.
利用显微硬度计、金相显微镜和X射线衍射仪测定了渗氮层的硬度梯度、层深、显微组织和相组成。
The hardness gradient, depth, microstructure and phases of nitrided layers were measured with Microhardness Apparatus, Microcopy and X-ray diffractometer.
碳氮共渗工艺选择不当，共渗层过深，表面出现壳状碳氮化合物、内氧化等缺陷组织是造成其断裂的主要原因。
The unsuitable carbonitriding process, internal oxidation, over deep depth of carbonitrided layer and crust like C N compound on the surface are the main reasons to cause fracture.