介绍了6063铝合金建筑型材的生产工艺。对其淬火敏感性、停放效应和制品的典型缺陷进行了讨论。
The production process of architectural 6063 aluminum alloy profile is introduced. The quenching sensitivity, keeping effect and typical defects of 6063 aluminum alloy profiles are discussed.
结果表明，尖角效应引起的应力集中和热处理淬火加热温度偏高是导轨端面产生裂纹的主要原因。
The results show the stress concentration caused by acute angle effect and the high temperature are the primary cause of producing crack.
对其淬火敏感性、停放效应和制品的典型缺陷进行了讨论。
The quenching sensitivity, keeping effect and typical defects of 6063 aluminum alloy profiles are discussed.