并数值计算了普通循环水冷结晶器与喷淋冷却结晶器的冶金参数。
The metallurgical parameters of the conventional recirculating water cooling and the spray cooling molds have been calculated respectively.
本发明解决了现有的结晶器因水冷分布不均，致使铸锭因应力集中产生铸锭裂纹的问题。
The invention solves the problem that cast ingot produces cracks caused by stress concentration as the existing crystallizer is not even in water-cooling distribution.
一旦中间包内的钢水达到规定的高度，水口就被打开，钢水注入放在托架上有内部水冷装置的结晶器内。
Once a predetermined steel level is attained in the tundish, nozzles are opened and the molten steel feeds the open-ended mould set in a frame with internal water-cooling.