踏面斜裂纹及断口的宏观形貌和理化检验与分析表明，踏面斜裂纹伤损属于滚动接触疲劳裂纹伤损类型。
The macro profile and physicochemical examination of the tread oblique crack shows that the crack falls into the category of rolling contact fatigue type.
对失效铝合金管进行了宏观形貌观察、材质检验、 断口微观形貌观察及应力分析。
The failure reason of the aluminum alloy tube was investigated by macroscopic and microcosmic appearance observement, quality of material test, the stress analysis.
通过宏观分析、断口分析、化学成分检验、金相检验和力学性能检测等方法，对汽车发动机曲轴断裂原因进行了分析。
The analysis of automobile engine crankshaft was conducted by macroscopic examination, fracture analysis, chemical composition analysis, metallographic examination and mechanical properties test.