本文对连铸小方坯结晶器的设计和操作参数作了一些说明。
This paper gave some remarks to the design and operational parameters of billet continuous caster mould.
经过几个月的实验,小方坯角部纵裂废品基本消失,取得了良好的冶金效果。
The longitudinal corner crack scrap of Billets disappeared almostly after four and half months test. Yielded the good metallurgical results.
本文通过对小方坯角部横裂纹的产生原因进行分析,并提出了相应的解决措施。
By analysing the causes of the transverse corner cracks of continuous casting billets, this article puts forward the relative measures to control the corner cracks.