利用扫描电镜断口分析及金相分析技术，分析了材料拉伸试件断口形貌及金相组织，初步探讨了材料的静态拉伸塑性变形机理。
The metallurgical structure and fracture morphology of the tensile specimens were investigated with SEM and metallurgical analysis, and the static tensile plastic deformation mechanism was researched.
少量铁素体的焊缝凝固裂纹断口上有许多小塑性区，有明显的韧窝。
Some plastic regions could be found and some dimples had been observed on the fracture surfaces of the solidification cracking of austenitic-ferritic weld metals.
在最佳超塑性条件下，断口中形成了大而深的空洞，晶界滑动和晶间断裂特征明显。
The deep and large cavities are formed on fracture surface and grain boundary sliding and intergranular fracture characteristic is obvious on the optimal superplastic deformation condition.