钢中的残余有害元素致使钢材产生红脆性表面裂纹和具有回火脆性倾向，并使耐热钢的热强性降低。
The residual deleterious elements in steel lead to products occurring red brittleness surface crack and temper brittleness, and lead to hot strength of heat resistant steel decreasing.
钢中的残余有害元素致使钢材产生红脆性表面裂纹和具有回火脆性倾向，并使耐热钢的热强性降低。
The residual deleterious elements in steel lead to the products occurring red surface brittleness crack and temper brittleness, and lead to the hot strength of heat resistant steel decreasing.
本文对淬火加回火渗碳钢的拉伸一拉伸疲劳断口进行了内裂纹的分析和研究。
Internal fatigue cracks occurred in the fracture of a quenched and tempered carburized steel specimen under tension-tension fatigue loads are discussed in this paper.