压痕试验 ( indentation test )是利用标准的洛氏硬度机之金刚石圆锥(C尺度)，试验荷重为150 kg，施压后于镀膜表面形成压痕，并借由光学显微镜，在100倍的放大倍...
基于368个网页-相关网页
The standard indentation test was done to Ni-Mn-Ga film with thickness about 400nm. Elastic modulus of the film was calculated as 3.79GPa while hardness was 252.92MPa.
对沉积在硅片上400nm厚的薄膜进行了标准压痕试验,得到薄膜弹性模量为3.79GPa,薄膜硬度为252.92MPa。
参考来源 - 铁磁形状记忆合金Ni·2,447,543篇论文数据，部分数据来源于NoteExpress
基于纳米压痕理论方法，对单晶铜进行了纳米压痕试验。
On the basis of fundamental nanoindentation theory, nanoindentation of single-crystal copper has been researched.
通过盘形滚刀侵入岩石的压痕试验得出岩石的跃进破碎参数。
According to the pressure trace test for measuring the intrusion of disc cutters into rock, the parameters of rock broken leaping forward are obtained.
利用纳米压痕技术对单晶铝作压痕试验，获得载荷-压深的加载和卸载曲线。
Nanoindentation experiments were made on single crystal aluminium, and load-depth loading and unloading curves were obtained.