针对45钢冷拔厚壁管存在内表面横裂纹问题,分析了其产生的原因。
The causes of inner transversal crack of cold-draw heavy wall pipe of 45 steel were analyzed.
生产实际应用表明,该模型对减少板坯表面横裂纹和角部裂纹有显著效果。
The practice shows that the model can remarkably reduce transversal and corner cracks on slab surface.
研究表明,铸坯表面温度落入钢的第三次脆性温度区是造成铸坯表面横裂的一个重要原因。
The research results showed that the slab surface temperature dropping into the third brittle zone played an important role in causing transverse crack formation of microalloyed slab.
研究表明,铸坯表面温度落入钢的第三次脆性温度区是造成铸坯表面横裂的一个重要原因。
The research results showed that the slab surface temperature dropping into the third brittle zone played an important role in causing transverse crack formation ofm...
研究表明,铸坯表面温度落入钢的第三次脆性温度区是造成铸坯表面横裂的一个重要原因。
The research results showed that the slab surface temperature dropping into the third brittle zone played an important role in causing transverse crack formation of microalloyed slab. E…
以永兴钢厂现场生产数据为基础,研究各种工艺参数对HRB335钢种表面横裂纹的影响。
Effects of various process parameters on the surface cracking of steel grade HRB335 have been studied with the on-site data acquired from Yongxin Steel-making Plant as the basic material.
以永兴钢厂现场生产数据为基础,研究各种工艺参数对HRB335钢种表面横裂纹的影响。
Effects of various process parameters on the surface cracking of steel grade HRB335 have been studied with the on-site data acquired from Yongxin Steel-making Plant as the basic material.