研究了高锰钢合金化对组织的影响。
The effect of alloying high manganese steel on microstructure has been studied.
介绍高锰钢斗齿焊接的一种新方法。
A new method of welding high Mn steel bucket teeth was introduced.
这种自行车是用锰钢制造的。
特点:举升机构采用高强度锰钢钜形管制作。
Features: the lifting mechanism adopts high strength manganese steel rectangular tube production.
对微合金化高锰钢衬板断裂原因进行了分析。
The fracture reasons of lining plate of microalloying high Mn steel have been analyzed.
可以堆焊在锰钢上。
球磨机采用橡胶衬板代替锰钢材板具有许多优点。
It was benifit to use the rubber lining instead of the manganese steel lining in the ball crusher.
用于露天煤矿大型托轮的高锰钢属于难加工材料。
Austenitic manganese steel, which serves as large riding wheel at open-cut coal mine, belongs to hardworking material.
高锰钢堆焊,适用于破碎机等受冲击磨损部位的堆焊。
Used for surfacing welding high-Mn steel, including various part of heavy impact abrasion resistance.
其成分特征是碳含量在共析点左右的高碳低锰钢轨钢。
The main characteristics of the rail steel are low manganese and high carbon which content is being closed to eutectoid.
经过分析,确定了组织和力学性能最佳的一种改性高锰钢。
From the subsequent analysis, one kind of modified Hadifield-steel with good microstructure and optimal mechanical property was obtained.
钻头采用锰钢制造,经过特殊加工处理,适用于各种地质环境。
Bit using manganese steel manufacturing, through special processing, are suitable for all kinds of geological environment.
对高锰钢微合金化提高耐磨性的机理及有关工艺作了详细介绍。
The mechanism that increases the wearability for microalloying of high manganese steels and the concerned processes is introduced in this paper.
通过冲击试验,研究了水韧处理质量对高锰钢低温韧性的影响。
The effects of water toughening quality on the toughness at low temperature of high-manganese steel was studied using impact -tests.
在伴有冲击的热强碱腐蚀磨损工况,高锰钢有过早失效的危险。
Under hot concentrated caustic impact-corrosion-abrasion conditions high Mn steel may be failure in earlier time.
结果表明:铸造复合中锰奥氏体钢的耐磨性是高锰钢的5.41倍。
The results show that the wear resistance of casting composite medium manganese steel is 5.41 times that of Hadfield steel.
只要材料成型及控制工艺得当,用该成分的高锰钢生产衬板是可行的。
It is feasible that use this high Mn steel to produce lining plate so long as the forming and controling processes of materials are suitable.
采用元胞自动机与有限元相耦合的方法模拟厚断面高锰钢铸件凝固组织。
Solidification microstructures in heavy section high manganese steel casting were simulated using coupling cellular automaton(CA)and finite element method(FEM).
而假如变紫红色:无磁性的为高锰钢,有磁性的通常为通常钢或低合金钢。
And if the purple red: nonmagnetic as high manganese steel, magnetic usually usually steel or low-alloy steel.
改性奥氏体锰钢适用于冲蚀磨损、凿削磨损以及高应力磨损等工况条件下。
The modified austenitic manganese steel is suited for the operating condition of impact-corrosive wear, chisel-cutting wear and high stress wear.
研究了铬加入高锰奥氏体钢中后,原奥氏体高锰钢组织中出现的一种新相。
The austenite manganese steel when added to with Chromium element appears a new phase.
利用传统的喷丸技术对高锰钢表面喷丸处理,研究材料表层的组织结构特征。
The high manganese steel was processed by the conventional shot peening technology, and the surface microstructure was characterized.
通过理论分析和系列冲击试验,对高锰钢出现的低温脆性损坏进行了分析研究。
The study of damage of low temperature brittleness on high manganese steel has been carried out by theoretical analysis and a series of impact tests.
采用进口高强度锰钢和国际领先的一次成型铸造技术,耐磨、抗压、使用年限长。
Adopting the imported high strength manganese steel and international lead step molding technology, wear-resistant anti-pressured and long service life.
结果表明,在相同试验条件下低碳高合金钢的冲击腐蚀磨损性能要优于高锰钢的。
The results show that the resistance of low carbon high alloy steel is better than that of the high manganese steel under the same test condition.
采用压缩试验方法,就合金元素对铸态锰钢的加工硬化性能的影响作了系统试验;
The effects of alloying elements on the work hardening ability of as cast manganese steels wre carried out by means of compressive tests.
消失模铸造生产大型高锰钢颚板,并按设计的工艺要求进行生产,利用余热水韧处理。
Large scale high manganese steel alligator board produced by EPC process can meet the request of design, and use with hot remained water toughening treatment.
研究了合金化变质改性对提高奥氏体锰钢基体碳含量,改变析出碳化物形态及分布的影响。
In this paper the effect of alloyed modification for carbon content, carbide shape and distribution in austenitic manganese steel has been studied.
破碎壁、轧臼壁采用进口高锰钢制作,极大降低磨耗,使用年限提高70% - 90%。
Broken walls, rolling ace tabular wall made of imported high-manganese steel, greatly reducing wear, the useful life by 70% -90%.
装机试验表明,该材质锤头使用寿命比高锰钢高,特别是铸态中锰钢锤头寿命可提高60%。
The field tests indicated the service life of this alloy steel hammer is higher than high manganese steel, especially the cast can be raised to 60%.