因此，需要提供一种锭模来铸造板坯，以克服前述缺陷。
Thus, it is necessary to achieve an ingot mold to cast slabs to overcome the foregoing drawbacks.
锭模材料？
本文从理论上分析了采用锭模吹氩对提高镇静钢质量的作用。
This paper has theoretically studied the effect of blowing Ar into molds on improving killed steel ingot quality.
现有技术中已知的有用于铸造金属条特别是钢条的多种锭模。
Numerous types of ingot molds used for casting metal strips, in particular steel, are known in the state of the art.
讨论了锭模的高宽比、绝热板材质对凝固位置及缩孔疏松的影响。
It is discussed that adiabatic material, as well as ratio of height and width effected solidification, shrinkage cavity and shrinkage porosity.
然而，这种锭模能够生产具有厚度的板坯，仍然需要相当大的机器用于生产线。
Such ingot mold, however, is able to produce slabs with a thickness that still requires considerably large machinery for the production line.
本实用新型的目的在于提供一种合金大锭模芯，以克服合金大锭不便于桥式吊车机械手抓吊的弊端。
Objective of the utility model is to provide an alloy big ingot mould core to overcome the problem that alloy big ingot is not suitable for gantry crane manipulator grasping.
一种用于将熔融金属从容器传送入浇包、锭模、流槽、供料压铸机或其它结构中的一个或多个的系统。
A system for transferring molten metal from a vessel and into one or more of a ladle, ingot mold, launder, feed die cast machine or other structure is disclosed.
结果证明，换底锭模寿命比旧式锭模延长5倍、费用降低73%，并可基本上消除合金的缩孔、缩松缺陷。
The results show that the new mould′s life is more than 5 times than that of former one, the cost is reduced by 73%, and the shortages such as shrinkage pipe…
这些锭模可以生产板坯，根据所使用的各种方法，该板坯经历多次有时与表面处理和机械加工相关的厚度减小。
These ingot molds can produce a slab which is subjected to a number of thickness reductions, sometimes associated with surface treatments and machining, depending on the various processes used.
结果，除了湍流更少之外，还可以在锭模的进给区域获得更好的排放流，熔化钢铁的排放装置位于该进给区域。
As a result, it is possible to get a better discharge flow in the feeding zone of the ingot mold where the discharge device of molten steel is placed, in addition to less turbulence.
实验结果表明，使用性能良好的锭模耐火涂料在低剪切条件下，应具有较大的表现粘度与屈服应力，以及较小的塑性粘度和适当的触变性。
The results show that the coatings with good application properties have larger apparent viscosity , higher yield stress , lower plastic viscosity and proper thixotropy at lower shear rate.
实验结果表明，使用性能良好的锭模耐火涂料在低剪切条件下，应具有较大的表现粘度与屈服应力，以及较小的塑性粘度和适当的触变性。
The results show that the coatings with good application properties have larger apparent viscosity , higher yield stress , lower plastic viscosity and proper thixotropy at lower shear rate.