钢轨打磨可以有效解决钢轨的疲劳伤损。
The rail grinding can solve the fatigue damage of the rail effectively.
结果表明,掉块缺陷的形成是由于钢轨滚动接触疲劳伤损所致。
The result shows that rolling contact fatigue failures caused swap block defects of rail.