文章中列出了切实可行的钝化液配方。
The practical formulation of passivation solution is also given.
阐述了钝化液中各成分的作用及工艺条件的影响。
Functions of the main components and the effect of operating conditions on chromated film were described.
另外探讨了钝化膜的形成机制及一次钝化液的调整和维护。
In addition, the formation mechanism of passivation film, the adjustment and maintenance of passivation solution were also discussed.
结果表明,通过苯骈三氮唑系钝化液的处理可以明显提高铜合金的耐蚀性能。
The experimental results indicate that the treatment process of copper alloy using benzotriazole can improve the corrosion resistance greatly.
本发明涉及提供一种马氏体、铁素体不锈钢无铬强力钝化液的制备方法及应用。
The invention relates to a method for preparing chromium-free intensified passivation solution for Martensitic stainless steel and ferritic stainless steel and an application thereof.
给出了镀锌层银盐黑色钝化的工艺流程及配方,介绍了钝化液中各组分的作用。
The process flow and formulation of silver-salt black passivation of zinc electroplate were presented, and the functions of the different components in passivation solution were introduced.
本发明方法既可以提高镀镍层的抗腐蚀能力,同时也有效地较少了钝化液对环境的污染。
The method can improve the corrosion resistant capability of the nickel plating layers and simultaneously effectively reduce the environmental pollution of the passivation solution.
实验中采用的钝化剂具有对环境污染小、成本低、活性镁损失小、钝化液可循环使用等特点。
Passivating agent in test is with many characters like cost low, and Mg damage small and recycle use of passivating fluid.
在钝化历程中应严酷控制钝化液中氯离子含量,所用钝化用化学质料对氯离子都有限量要求。
Should be strict control in the passivation process of chlorine ion in the passivation solution, the passivation with chemical material used for chloride ions are limited.
研究结果表明,采用该种钝化液获得的钝化膜油黑发亮,色泽均匀,耐蚀性及耐磨性好,附着力强。
Influences of components in the passivating solution on film-forming rate and corrosion resistance of passive film we…
采用胶体电解质技术,绝无酸液浓度层化问题,完全消除因浓度层化引起的极板腐蚀和钝化现象。
It has adopted colloid electrolyte technology, avoiding density stratification problem of acid solution and eliminating plate corrosion and passivation caused by density stratification.
该文主要研究热处理钝化扁豆液中胰蛋白酶抑制子的方法。
This paper researched a method of heat treating to inactivate trypsin in dolichos lablab.
当混凝土的孔隙液相碱度降低到11.5以下时,钢筋钝化膜遭到破坏。
Deactivated film of reinforcing bar is destroyed when degree of alkalinity in pore fluid of concrete is lowed 11.5.
韭菜样本用微波炉加热处理,使酶钝化消除含硫基质干扰,然后用乙腈提取、逆固相分散净化,用反相高效液相色谱-二极管阵列检测器检测。
Then the pretreated samples were extracted with acetonitrile, further cleaned up by reverse solid phase dispersion, and analyzed by reversed phase HPLC with diode array detector (DAD).
羟基乙叉二膦酸酸洗后预膜液的选择较少有人研究,而适当的预膜钝化是防止酸洗后金属表面返锈的必要措施。
There is little study on the selection of liquid of pre - filming after the acid wash by hydroxy ethidine phosphonic acid (HEDP).
羟基乙叉二膦酸酸洗后预膜液的选择较少有人研究,而适当的预膜钝化是防止酸洗后金属表面返锈的必要措施。
There is little study on the selection of liquid of pre - filming after the acid wash by hydroxy ethidine phosphonic acid (HEDP).