对在低循环疲劳试验过程中破裂的某型机低压涡轮盘组件的残骸进行了材质和断口分析。
The materials and fracture surfaces of a low pressure turbine disk assembly that was broken during LCF testing were examined. The fracture of the LP turbine disk was resulted from low cycle fatigue.