腐蚀介质和介质温度对沟槽腐蚀敏感性系数无显著的影响。
The corrosive solution and test temperature have no apparent effects on the grooving corrosion sensitivity coefficient.
本文首先研究了不同腐蚀介质下混凝土保护涂层的吸水行为。
Firstly, in this paper water absorption of concrete protective coatings hi different corrosive medium is studied.
外壳和介质浸润部分由不锈钢制成，可以抵抗化学腐蚀介质。
Case and wetted parts made of stainless steel are resistant to chemically aggressive media.
针对碱性腐蚀介质下水电解槽的工作条件，设计了其密封结构。
The sealing structure was designed according to the working conditions of water electric tank in condition of alkaline erosive medium.
研究了1420合金在不同腐蚀介质环境下的预腐蚀疲劳性能。
The fatigue performance of pre-corroded 1420 alloy in different corrosion environment was studied.
方法采用目测法对不同腐蚀介质作用后的器械锈蚀情况进行观察。
Visual method was used to observe corrosion condition of instruments after exposure to different corrosive mediators.
在拉应力和腐蚀介质的共同作用下引起设备开裂的现象时有发生。
Affected by tensile stress together with corrosion medium, cracking phenomenon in equipment occasionally happens.
硫酸作为强腐蚀介质之一，硫酸是用途非常广泛的重要工业原料。
Sulfuric acid as one of strong corrosive medium, sulfuric acid is the use of a very wide range of important industrial raw materials.
不锈钢毓还可以输送任意浓度的酸、碱液、氧化剂及其他腐蚀介质。
Yu stainless steel can also transfer any of the concentration of acid, lye, oxidants and other media corrosion.
结果表明，陶瓷涂层能大幅度提高基体在各种腐蚀介质中的耐蚀性。
The results indicate that ceramic coating can greatly improve the corrosion resistance of matrix in various corrosive media.
实验表明，在腐蚀介质中进行交流电解是铱材金相制作的快捷之路。
It is shown that the AC electrolytic corrosion process in a corrosive is a easy way to prepare metallographic specimens of iridium material.
普通板式换热器在高温、高压和腐蚀介质等情况下的使用受到了限制。
The use of general plate heat exchanger is limited due to high temperature, pressure environment and erodent medium.
分层腐蚀介质、分段腐蚀介质和其他钢样也影响电位和电流分布情况。
Besides, layered or subsection corrosion medium and other steels can also influence in the distribution of potential or current.
从材料、结构角度对疲劳荷载和腐蚀介质的耦合作用进行了总结与分析。
The coupling effect of fatigue and erosive ions is introduced on the level of material and structure.
同时还介绍了根据腐蚀介质、温度选择底漆、胶合剂、面漆等的搭配原则。
The selection of priming paint, glue bond, block material and surface paintbased on the nature of the corrosive medium is discussed.
无严重影响触头盒绝缘的气体、蒸汽、灰尘及其它爆炸性和腐蚀介质的场所。
NO gas , wapor or dust that may severely affect the insulation of contact box, no explosive or corrosive substance.
结果表明：改性后的产品在中性、酸性腐蚀介质中，对钢材有较好的缓蚀作用。
The result showed that the modified product had good corrosion inhibition for steel in neutral or acid corrosive media.
通过失重法、电化学方法研究低合金钢镀膜前后在不同腐蚀介质中的耐蚀行为。
The anti corrosion behavior in different corrosion environments was studied by weight loss test and electrochemical method.
介绍了储罐出口管线软连管的选用及在输送腐蚀介质时如何进行合理的材料选择。
This paper introduces the type selection of compensator in the outlet pipeline of storage tank and rational selection of material as transporting corrosive media.
腐蚀介质到达基体时，将发生电偶腐蚀，铝涂层会作为牺牲阳极保护基体免受腐蚀。
Once corrosive solution arrived at the substrate, galvanic corrosion occurred, and aluminum coatings acted as the sacrificial anode protecting the steel substrate from corrosion.
避免重腐蚀介质长期浸泡地板漆膜，扩散轻率腐蚀性酸和碱等，请及时清洁酸和碱介质。
To avoid heavy corrosion medium long-term immersion floor paint film, the proliferation of lightly corrosive acid and alkali, etc.
稳定操作条件，控制各工艺指标，隔离腐蚀介质等可防止腐蚀裂纹的产生或进一步扩展。
The emergence of the corrosion crack and the further expanding was protected by the means of smoothing the operation condition, controlling the technology indexes, isolating the corrosion medium.
不锈钢酸洗用酸洗液是多种酸的混合物，腐蚀性强且具有氧化性，腐蚀介质温度较高。
Pickling solution for acid pickling of stainless steel is a mixture of various acids which possess strong corrosiveness and oxidization.
避免重腐蚀介质长期浸泡地板漆膜，扩散轻率腐蚀性酸和碱等，请及时清洁酸和碱介质。
To avoid heavy corrosion medium long-term immersion floor paint film, the proliferation of lightly corrosive acid and alkali, etc., please clean the acid and alkali media.
分析试验结果表明，这些陶瓷涂层大幅度提高了基底金属在腐蚀介质及氧化环境中的寿命。
The results indicate that the ceramic coating films increase drastically the lifetime of the substrate metal in corrosive media and oxidizing atmosphere.
通过这种方式，腐蚀产物在宏观孔隙中形成致密的微观结构，阻止腐蚀介质对界面的破坏。
By this way, the microstructure of corrosion products in macro-pores became compact and the destruction of corrosion medium to interface was inhibited.
在第4章，参照相关标准，并根据腐蚀介质的特殊性，创造性的设计了试验室金属腐蚀试验。
In chapter 4, according to the related standards and the particularity of the caustic medium, the paper puts forward a creationary laboratory metal corrosion test.
结果表明，其本质是腐蚀介质穿透包铝层，使板材中心的合金产生晶间腐蚀，引起表皮肿胀。
The analysis result indicates that the corrosive penetrate through aluminium cladding and the interior alloy occurs intergranular corrosion. Therefore partial surface of plate swells.
基本上，这些需求的钢管材料，都具有足够大的强度，韧性，良好的焊接能力以及耐腐蚀介质。
Basically, those steel pipe materials which, with adequately high strength, show sufficient toughness, good welding behaviour and resistance to corrosive media are in demand.
污水处理工程在运行中经常受到气、液相腐蚀介质的破坏，严重地影响其使用功能和结构安全。
When sewage disposal engineering runs and contacts corrosive substances in gaseous or liquid state, its construction will be destroyed and influenced its function.