采用三官能度的聚氧化丙烯醚醇、聚乙二醇,合成了吸水膨胀率在0~200%的聚氨酯弹性体。
Using tri-functionality polyoxytrimethylene alcohol ether and polyethylene glycol, synthetize polyurethane elastomer with water absorption expansion rate of0~200%.
以聚氧化丙烯二醇和甲苯二异氰酸酯、一缩二乙二醇等为主要基体材原料,以联二脲(LDA)、聚磷酸铵(APP)作为阻燃剂,制作了聚醚聚氨酯弹性体。
Polyether polyurethane elastomer material was prepared based on polypropylene oxide glycol, toluene diisocyanate (TDI) and DEG as main base meterial, LDA and APP as flame retardants.
通过以含醚键的聚(氧化丙烯-氧化乙烯)为主体,与二氧化锡溶胶复合,制备了一类可用于尼龙的抗静电剂。
Poly (propylene oxide-ethylene oxide) containing ether linkage was used to make complexes with stannic oxide sol, thus producing a kind of anti-static agent for nylon resins.
本文研究了聚氧化乙烯(peo)和丙烯腈(AN)在水溶液中的超声共聚。
PEO-AN block copolymers were synthesized in aqueous solution by using ultrasonic technique.
本文研究了聚氧化乙烯(peo)和丙烯腈(AN)在水溶液中的超声共聚。
PEO-AN block copolymers were synthesized in aqueous solution by using ultrasonic technique.