强流脉冲电子束轰击可以实现316L不锈钢表层的选择性净化，表面织构化及表面快速钛合金化，从而提高不锈钢的耐蚀性。
The main results are summarized as follows:1, HCPEB bombardment induces the selective purification on the top surface of 316L stainless steel, surface texturation and rapid surface alloying with Ti.
重点研究了铝的纯度、均匀化制度、热轧温度、冷轧及中间退火对最终退火后箔材形成立方织构的影响。
The emphasis is put on effect of purity homogenization, hot rolling temperature, cold rolling and medium annealing on cubic texture of finally annealed foil.
选取低硅无取向硅钢常化态板材，分别在不同速比下进行异步轧制，考察了速比对低硅无取向硅钢冷轧织构的影响。
The effect of speed ratio on the texture of non-oriented cold rolled low silicon steel sheet was investigated after cross shear rolling at different speed ratios.
结果表明：热轧及常化退火工艺对硅钢冷轧织构有显著的影响。
The results show that hot rolling and normalizing annealing processes have significant influence on the cold_rolled texture of silicon steel.
常化处理使组织均匀化并增加有利于磁性提高的织构组分；
Normalizing treatment makes microstructure uniform and increases component of favorable texture.
常化处理使组织均匀化并增加有利于磁性提高的织构组分；
Normalizing treatment makes microstructure uniform and increases component of favorable texture.