同时采扫描电镜对喷嘴磨损表面进行了分析。
Wear surface of nozzle were analysed with scanning electron microscope.
研究了断裂方式对磨损表面剥落和耐磨性的影响。
The influence of fracture mode and wear surface pullout on wear resistance was studied.
用碳化硅挤嵌磨损表面，是一种新的表面处理工艺。
It's a new technology to treat a wear surface by impregnating in silicon carbide.
函数法计算磨损表面轮廓的分形维数和尺度系数。
Fractal dimension and scale coefficient of surface profiles are calculated using structure function method.
采用扫描电子显微镜观察分析了复合材料磨损表面形貌。
The worn surfaces of the composites were observed on a scanning electron microscope.
利用扫描电子显微镜对材料的磨损表面进行了观察和分析。
And the worn surfaces morphologies of the reinforced PTFE composites were examined with scanning electronic microscopy (SEM).
第二章分析了刀具前刀面、后刀面和边界磨损等磨损表面的特征。
The second chapter analyzes the characters of rack face, flank face and boundary wearing.
磨损过程中在磨损表面覆盖的氧化物层对涂层起到保护和减磨作用。
During wear process oxide layer formed and covered the wear surface, which protected the wear surface and decrease the wear.
用XPS研究了渗硼层磨损表面的成分、元素价态及其随深度的变化。
The elemental composition and valence state of the elements and their changes with the variation of depth were investigated by mains of XPS.
结果表明：所制备的修复剂对磨损表面具有明显的修复作用，形成了修复层。
The results showed that the additive had evident repairing action and formed repairing layer on the wear surface.
为了区分磨损表面图像中的磨损目标与背景，本文引入了图像边缘提取技术。
The paper introduces image edge extraction technology in order to make a distinction between abrasive objectives and settings on the surface of abrasive image.
堆焊或修复低碳钢、中碳钢及低合金钢磨损表面如车轴、齿轮和搅拌机叶片等。
For surfacing welding or repair the wear out face made by low carbon steels and middle carbon steels, as axle, gear and blade of mixer.
用扫描电子显微镜和X射线光电子能谱仪观察分析了磨损表面形貌和元素化学形态。
Worn surface morphology and element chemistry configuration of steel ball were analyzed by means of X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM).
通过用扫描电镜对磨损表面形貌进行的观察分析，探讨了复合涂料涂层的磨损机理。
By using SEM to examine the worn surface morphology, the wear mechanisms of these coatings were explored.
通过道路试验研究，分析了汽车正时套筒链的磨损机制及销轴和套筒的磨损表面形貌。
By the experiment research on road running test of timing bushing chains for automotive engine, its wear mechanism and the worn surface of pins and bushings were analyzed.
基于磨损表面的分形表征、经典接触理论和磨损理论，建立了磨合磨损预测分形模型。
Based on the fractal characterization of worn surfaces, classical contact mechanics, and wear theory, a fractal model for predicting wear during the running in process was developed.
开发了一种基于激光共焦显微镜和图像处理技术的研究磨损表面及表面参数的新方法。
A new approach to gain surface parameters to characterize worn surfaces using confocal laser scanning microscopy and image processing technique was proposed.
采集机械磨损表面形貌轮廓曲线来分析器械部件的使用状态是检验检测工作的常用方法。
By collecting topography profile of worn surface, it is common method that using status of appliance parts is analyzed.
用扫描电子显微镜(sem)和X射线光电子能谱仪(XPS)对钢球磨损表面进行了分析。
The worn surfaces of the steel balls were analyzed by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS).
运用扫描电镜观察了这几种材料在泥沙磨损条件下的磨损表面形貌，分析了它们的磨损机理。
The wear surface morphologies were surveyed by scanning electron microscope (SEM) and wear mechanism was analyzed under the sand slurry wear condition.
即将发生粒子剥落的铝硅合金磨损表面区域，由表及里为复合层、变形层相未变形母体材料。
The worn layer of Al-Si alloy where only wear debris are going to delaminate is composed of composite layer, deformed layer and undeformed parent material from the surface to the inside.
通过磨屑形貌分析和对磨损表面的观察与分析所得的关于复合材料的磨损机制的结论是一致的。
The conclusion on the wear mechanism of the composite by the debris topography analysis is coincident to that of the SEM analysis on the worn surface.
对冲击磨损试验后试样进行了失重测量，并用SEM分析磨损表面形貌，用OM观察金相组织。
The mass loss after impact-wearing was measured, the morphology on the wear surface of the steel was analyzed by SEM, the microstructure was observed by OM.
用三坐标表面粗糙度仪测量了磨损体积，利用脉冲电位评价磨损产生的新生面与磨损表面的关系。
The wear volume was measured with 3D measuring instruments and the relationship between the fresh surface that fretting wear produces and worn surface was evaluated with the potential pulse method.
用三坐标表面粗糙度仪测量了磨损体积，利用脉冲电位评价磨损产生的新生面与磨损表面的关系。
The wear volume was measured with 3D measuring instrument and the relationship between the fresh surface fretting wear produces and lost surface was evaluated with the potential pulse method.
按一般概念，实验室磨损试验与实物试验所获得的磨损表面形貌如果相似，就认为实验室试验是有效的。
In common sense if the topography similarity of worn surface is obtained from laboratory test and field test, then the laboratory test is worthy. But it is not always true.
应用分形理论对弹头磨损表面形貌进行了研究，研究表明，其表面磨损形貌的不规则和随机分布性具有分形特征。
The topography of bullet surface wear was studied by using fractal theory. The irregularity and random distribution of its surface wear show the fractal characteristics.
借助SEM及EPMA等手段对磨损表面及亚表面和粘着磨损的材料转移情况进行了观察和分析，并对磨损机制进行了讨论。
The worn surface and sub-sarface. of both composite and its base alloy were examined by SEM and EPMA with special attention on the materials transfer and the wear mechanism.
通过对不同基体组织轧制白口铁的金相组织、磨损表面和机械性能的分析，研究了具有不同基体组织轧制白口铁的磨损机理。
The abrasive mechanism of rolled white cast iron with various matrixes are studied by investigating the microstructure, abrasive surface and mechanical properties of specimens.
采用多功能SRV试验机考察了超细高岭土在菜籽油中的高温摩擦学性能，并利用表面轮廓仪对试块的磨损表面形貌进行观察。
High temperature tribological behaviors of superfine kaolin in colza oil were tested with SRV machine, and wear surface was observed by surface profiler.