而浸渍树脂的碳毡硅化处理后的显微组织特点是反应生成的碳化硅颗粒粒径及分布均不均匀。
As for the impregnated carbon felt, the reaction-formed SiC particles were nonuniform in size and distribution, and the smaller SiC particles would dissolve with the increase of sintering time.
结果表明，随着基体中硅含量的增加，复合材料的磨损率大大降低，另外，致密化处理可进一步改善铝基复合材料的耐磨性能。
It was found that the wear rate evidently decreased with the increase of silicon content. Densification treatment could further improve the wear resistance of the aluminum based composites.
通过在中硅耐热铸铁中添加不同组合的合金元素稀土、铜、钛使其合金化，经过孕育和球化处理，得到铁素体+珠光体+球状石墨的金相组织。
Adding different alloy combination of re, copper and titanium, then through gestation and nodulizing disposal, we got the fine texture of ferrite pearlite and spheroidal graphite.
报道了对多孔硅进行后处理的一种新方法，即真空中微波等离子体辅助的硫钝化处理。
A new method for post treatment of porous silicon, sulfur passivation by microwave plasma assistance in vacuum, is reported in this paper.
实施结果表明，采用碱化处理洗硅工艺可大大缩短洗硅时间，且洗硅彻底，经济效益显著。
Results show that the said technology can greatly shorten the silicon cleaning time duration, and the silicon cleaning to be perfectly thorough, economic benefits to be remarkable.
采用N2O和NH3等离子钝化技术对多晶硅薄膜表面和栅氧表面进行了钝化处理。
The surfaces of poly-Si thin film and gate oxide of thin film transistors were passivated using N2O/NH3 plasma.
这种材料还需经进一步纯化处理，生成半导体级或太阳能级多晶硅原料。
This material is further purified to semiconductor-grade or solar-grade polysilicon feedstock.
这种材料还需经进一步纯化处理，生成半导体级或太阳能级多晶硅原料。
This material is further purified to semiconductor-grade or solar-grade polysilicon feedstock.