采用电化学、失重和盐雾实验对铝管表面硅烷稀土复合膜的耐蚀性进行考察。
Corrosion resistance of aluminum tube surface with silane-rare earth composite coating was studied by electrochemical means, weight loss and salt spray test respectively.
同时通过中性盐雾实验、镀层结合力测试,研究和比较了不同基材上铑镀层的性能。
Various performance tests (neutral salt spray, metallic coating binding force) about rhodium plating on different substrate metal material were also studied.
以丙二胺改性天然虫胶为主要原料的涂料用于铜表面,通过盐雾实验表明:其防腐蚀性能得到很大的提高。
Coatings is prepared with propane diamine modified shell-lac as main raw material. Results of salt - spray test show that anticorrosion performance of these coatings has been improved a lot.
盐雾实验中,盐的浓度、大阴极小阳极的面积比以及阴极材料相对于镁阳极的尺寸是加速镁合金电偶腐蚀的重要因素。
The concentration of salt and the relative areas of the large cathode coupled with a small magnesium alloy anode have an important effect on the accelerated galvanic corrosion in salt spray test.
曾对此套作了耐候、耐湿热、耐盐雾、抑真菌、存放等性能实验。
Moisture and temperature test, Salt spraying test, Fungus test and Storing test.
极化曲线和中性盐雾腐蚀实验表明:钛合金耐腐蚀性能良好,腐蚀失重不明显。
Polarization curve and neutral atmosphere salt corrosion test showed that the corrosion resistant property of BT20 Ti alloy is excellent, and mass loss of both is not obvious.
极化曲线和中性盐雾腐蚀实验表明:钛合金耐腐蚀性能良好,腐蚀失重不明显。
Polarization curve and neutral atmosphere salt corrosion test showed that the corrosion resistant property of BT20 Ti alloy is excellent, and mass loss of both is not obvious.