本发明涉及一种冷冻生坯及其生产方法。
The invention relates to a frozen green blank and a manufacturing method thereof.
本文分析了园筒形陶瓷生坯干燥应力情况。
This paper analyses drying stress of cylindrical pottery blank.
该机生产的生坯采用热风旋转炉及隧道炉烤均可。
The green production with hot rotating furnace and tunnel stove roast.
该机生产的生坯采用热风旋转炉及隧道炉烘烤均可。
The green body made by this machine can adopt toast either at hot wind rotary stoves or the tunnel stoves.
温压工艺可达到比传统铁粉压块更高的密度与生坯强度。
Warm compaction process yields higher density and improved green strength over conventionally processed iron powder compacts.
即可成为饼干生坯，经烘烤做成各种中高档饼干、薄饼干等。
Can be made by baking cookies green, various high-grade cookies and cakes and wait.
研究了注射成形生坯厚度与缺陷产生的临界升温速度的关系。
The relationship between thickness of MIM green parts and critical heating rate was studied.
本文评述了粘结剂-处理材料的物理性能，生坯与烧结体的性能。
This paper reviews the physical, green and sintered properties of binder-treated materials.
料浆愈稳定，生坯密度愈高，微观结构愈均匀，但吸浆速度减慢。
The higher the suspension stability, the higher the green density, and the more homogenous the microstructure, but the smaller the permeation rate.
该机生产的生坯可配合我厂生产的热风旋转炉或隧道烘炉烤均可。
The green body made by this machine can adop toast either at not wind rotary stoves or the tunnel stoves.
烧结生坯，在含有氮气的气氛中并在吸氧剂的存在下进行所述烧结。
The sintering is conducted in an atmosphere containing nitrogen and in the presence of an oxygen getter.
测定了它们的冷压生坯密度、模拟生坯强度以及高频钎焊的结合力矩；
Green-pressing density, simulated green-pressing strength and bonding momental of high frequency brazing were assayed.
以制备金红石瓷为例，给出了陶瓷浆料的制备及陶瓷生坯的制造过程。
Preparation of titanium dioxide slurry was performed and the manufacturing process of the green ceramic body was given.
介绍了基体钢粉牌号和各种添加剂的数量与类型对生坯与烧结件性能的影响。
The influence of base ste el powder grade and the amount and type of various additives on the green and sintered properties is presented.
有机添加剂是流延料浆的关键组元，它们对料浆和流延生坯的性能有很大的影响。
Organic additives play a pivotal role in the tape-casting slurry. Different additives have various effects to the slurry and green tape.
用电容器级钽粉压成适于制作固体电解电容器阳极的坯块， 压缩测定其生坯强度。
The crush strength of pressed pellets of capacitor grade tantalum powder which is used for making tantalum solid electrolytic capacitor was tested.
利用X射线衍射分析方法，对湿压磁场成型的永磁铁氧体生坯晶体取向度进行了研究。
Degree of preferred orientation of hard Sr ferrite compacts molded with magnetic field was studied by X ray diffraction analysis.
在较低的固相含量和较高的离心加速度下，浆料的分离现象明显，生坯中出现密度梯度。
The mass segregation phenomenon became more obvious at lower solid content and higher acceleration and there were density gradient in green compacts.
研究了反应烧结碳化硅陶瓷的显微组织和性能与生坯碳含量、成型压力以及碳粉粒度的关系。
The effects of carbon content, moulding pressure, and carbon particle size of green body on microstructure and properties of reaction-bonded silicon carbide (RBSC) have been investigated.
用于桃酥饼干辊印脱模成形。将调粉机已调好的面团，经辊印成各种形状及不同克数的饼干生坯。
This machine is used for roller printing and forming of walnut sweet cake, which makes semi-finshed biscuits of various shape and weight through roller printing .
研究电解铜粉高速压制成形工艺，探讨冲击能量、压制次数对生坯密度、最大冲击力和脱模力的影响。
The effects of impact energy and impact times on the green density, the maximal impact force and the withdraw force of specimen were investigated.
研究电解铜粉高速压制成形工艺，探讨冲击能量、压制次数对生坯密度、最大冲击力和脱模力的影响。
The effects of impact energy and compaction methods on the green density, the maximal impact force, the withdraw force and the radial springback were discussed.
本机用于桃酥饼干辊印脱模成型，将调粉机已调好的面团经辊印，成各种形状及不同克数的饼干生坯。
This machine is used for stripping roller which makes semi-finished biscuits, will adjust molding machine has prepared by roller, dough into various shapes and different.
通过数学模型描述炭阳极生坯冷却过程，研究炭阳极冷却温度与冷却时间、冷却水温及成型温度间的关系。
The variation of the cooling temperature of the green carbon anode with the cooling time, the temperature of cooling water and the forming temperature has been studied by computing simulation.
连铸弯月面区域的凝固传热对初生坯壳的均匀形成、铸坯的表面质量以及连铸生产的顺利进行有重要影响。
The solidification and heat transfer in meniscus zone have deep influence on the formation of initial solidified shell, surface quality and smoothness of casting operation.
不合理的钢液流动行为，会影响夹杂物的上浮、气泡的分布、保护渣的熔化及铺展性能、初生坯壳的形成等。
An unreasonable liquid steel flow behaviors have an effect on inclusion flotation, bubble distribution, liquid mold flux fluid capability and spreadability, shell growth, etc.
随成型压力的增加，当保压一定时间、添加一定量助烧剂时，生坯密度随之增加，饱和磁化强度也相应提高。
With the increase of molding pressure, holding pressure for certain time and adding a certain amount of boric acid doping, the compact density and saturation magnetization correspondingly increase.
石墨电极生坯生产的压型工序中压型调速方法的选择及其速度控制的稳定性直接影响着石墨电极的产量和质量。
The way of velocity governing of graphite electrode extruder and the stability of velocity control can influence the product and the quality of graphite electrodes.
为保证绝缘子获得较高致密度而不变形，应尽量提高生坯密度，同时排蜡温度应低于该种玻璃的转变温度上限。
To insure more densification but deformation of glass beads, the green density should be increased, and the burnout temperature of binder should be below the toplimit of transformation temperature.
为保证绝缘子获得较高致密度而不变形，应尽量提高生坯密度，同时排蜡温度应低于该种玻璃的转变温度上限。
To insure more densification but deformation of glass beads, the green density should be increased, and the burnout temperature of binder should be below the toplimit of transformation temperature.