该球化剂应用于高炉冷却壁、轧辊等铸件上，可提高其心部力学性能。
The mechanical properties of core in the castings such as the cooling wall of blast furnace and the rolls are enhanced by using this nodulizer.
论述利用江西省离子吸附稀土矿研制镧镁硅铁合金-镧镁球化剂的概况。
The paper described the development of a La-Mg-Si-Fe nodulizer alloy from the ion-absorbed rare earth ore of Jiangxi province.
研究了镧镁球化剂的球化能力及其对球墨铸铁白口敏感性和抗衰退性的影响。
The nodulizing power of the La-Mg nodulizer and its influences on the chilling sensitivity of nodular cast iron and the property of anti-degeneration were studied.
该球化剂应用于高炉冷却壁，轧辊等关键球铁件上可提高抗拉强度和伸长率。
The properties of cores in the casts are enhanced when using this nodulizer in the key ductile iron casts, such as cooling wall of blast furnace and roller.
这种新型粉状球化剂具有合金球化剂不可比拟的优越性，有可能成为90年代的换代产品。
This kind of new powdered nodulizing agent possesses unsurpassed advantages over other alloy agents and it may become the substitute agent in 90's.
公司主要生产硅铁，硅粒，硅粉，球化剂，孕育剂，脱氧剂，碳化硅，增碳剂，等产品的重点企业。
The company mainly produces ferrosilicon, silicon particle, silica fume, nodulizer, inoculant, deoxidizer, silicon carbide, carbon agent, key enterprises and other products.
经过分析和试验，开发出一种新的高效球化剂和一种新的高效复合随流孕育剂，制定出铸态生产工艺。
By analysis and experiment, a new type of noduler with high efficient and a new type of high mixed in-flow inoculant have been developed, and the as-cast production was made.
应用钇基重稀土镁复合球化剂，铸造厚大断面高韧性球铁冷却壁，成功地获得了铸件中心部位铸态高性能。
The RE(Y)-Mg-Si-Fe nodularizer had been used to cast heavy sectioned high ductile nodular iron cooling wall castings.
研究了用含稀土量不同的球化剂生产单体铸造球铁活塞环时，稀土时石墨球数、石墨球径、碳化物数量的影响；
Effect of RE on nodule number, nodule diameter and carbide quantity is studied with nodulizers of different RE contents.
研究了球化剂中氧化镁含量对球化效果、球铁的显微组织和性能的影响，以及球化剂中所能允许的氧化镁临界含量的确定方法。
The influences of the MgO content of the nodularizing alloy on nodularizing effect, microstructure and mechanical properties of nodular irons, as well as the method to …
引起反白口的主要原因是残余镁量，特别是残余稀土量过高，防止措施是采用稀土含量较低的球化剂，提高球化处理温度和浇注温度。
Too high residual magnesium content, and especially too high residual rare earth content is the main reason causing reverse chill defect. So them…
介绍了一种利用台车连续炉，以红土镍矿为原料，煤粉为还原剂，生产镍铁金属化球团的方法。
This paper introduces a method of producing metallization pellet with laterite nickel ore as raw material and coal as a reductant in car bottom continuous furnace.
在实验的基础上，通过自主设计建成了新的转炉尘泥化渣剂球团生产线；
On the base of experiments , a new plant processing utilization of converter residue designed was set up.
探讨了复合孕育剂中铝量对含砷、锡、铅、钛铸铁石墨球化的影响。
An approach to the influence of aluminium content of inoculant on graphite spheroidization of cast iron containing as, Sn, Pb and ti was made.
采用气雾化法获得的合金粉，通过高能球磨处理工艺制备了扁平化磁性合金粉体雷达波吸收剂。
The atomized powder was improved by high-energy ball milling, then the radar absorbent of flattened magnetic alloy powder was made.
当空心微球包裹有药物、酶或催化剂时，可应用于药物缓释、酶固定化和催化剂领域。
The hollow microsphere can be applied in the fields of drug controlled release, enzyme fixation and catalyst when wrapping drug, enzyme or catalyst.
以自制的氨基化磁性纳米球为原料，戊二醛为交联剂，在氨基化磁性纳米球表面成功固载了组氨酸。
The histidine was covalently linked to the surface of amino-functionalized nanospheres using glutaraldehyde as cross-linker.
以自制的氨基化磁性纳米球为原料，戊二醛为交联剂，在氨基化磁性纳米球表面成功固载了组氨酸。
The histidine was covalently linked to the surface of amino-functionalized nanospheres using glutaraldehyde as cross-linker.