结果表明，聚丁二烯橡胶的焦烧安全性较好；
The results showed that the scorch safety of polybutadiene rubbers was good;
原材料可以是焦烧胶、硫化流失胶边和不合格的硫化制品。
The material can be scorched rubber, flash overflow and unacceptable vulcanized product.
采用复合助剂A作改性剂来改善阻尼橡胶的焦烧性能和溶解性能。
The compounding agent A is used as modification agent to improve the scorching and solubility property of damping rubber.
硫化温度的提高会缩短焦烧时间和正硫化时间，但有使交联密度下降的趋势。
With the increasing of cure temperature, the scorch time and optimum cure time decreased, but the crosslink density had a tread of decreasing.
与丁基橡胶相比，BIIR焦烧时间和正硫化时间明显缩短，硫化速度大大提高。
Besides the scorch time and optimum cure time of BIIR were shortened considerably while its curing rate increased obviously.
结果表明，白炭黑能加速CR/TPI并用胶的焦烧性能，同时降低了胶料的硫化速度。
The results show that with the increase of the amount of silica, the scorching time and optimum cure time of CR/TPI compounds are shortened.
结果表明，随着再生IIR用量的增大，胶料的门尼焦烧时间逐渐缩短，物理性能变化不大；
The results showed that the Mooney scorch time of rubber compound reduced as the addition level of reclaimed IIR increased, but the physical properties changed little;
结果表明，随着防焦剂CTP用量的增大，胶料的焦烧时间延长，硫化速率和物理性能变化不大；
The results showed that the scorching time of bead chafer compound extended without any adverse effect on curing rate and physical properties as the addition level of CTP increased;
结果表明，TBSI用作NBR硫化过程促进剂时，焦烧时间长，硫化胶强度高，但硫化速度较慢。
The results showed that as the accelerant of NBR in vulcanization, TBSI had much more scorching resistant time and higher vulcanization degree, but lower vulcanization rate.
结果发现：一羟基或羧基化合物能提高氟橡胶混炼胶的防焦烧性，并对压缩永久变形和拉伸强度等有一定的改善。
The results showed that the compound could improve the scorch safety the compression set and the tensile strength of fluororubber compound.
结果发现：一羟基或羧基化合物能提高氟橡胶混炼胶的防焦烧性，并对压缩永久变形和拉伸强度等有一定的改善。
The results showed that the compound could improve the scorch safety, the compression set and the tensile strength of fluororubber compound.
试验结果表明，纳米氧化锌可延长胶料的焦烧时间，提高硫化胶的拉伸性能和耐磨性能，硫化胶的耐老化性能也较好；
The test results showed that the scorch time of rubber compound ex tended by adding nano-zinc oxide, and the tensile strenght, abrasion resistance a nd aging property of its vulcanizate improved;
本论文基于国内实际生产情况，重点研究了内胎生产过程中经常遇到的严重影响产品质量的两大难题，即焦烧及接口开。
Based on national practical situation in the paper tire tube process's main problem such as scorch life and butt joint, which affect severely tire tube's quality was mainly studied.
本论文基于国内实际生产情况，重点研究了内胎生产过程中经常遇到的严重影响产品质量的两大难题，即焦烧及接口开。
Based on national practical situation in the paper tire tube process's main problem such as scorch life and butt joint, which affect severely tire tube's quality was mainly studied.