微波能是一种清洁型的新型能源,利用微波的热效应进行磁铁精矿微波烧结是一项全新的课题。
Microwave energy is a clean energy, and microwave sintering of magnetite concentrates is a new subject by microwave heating effect.
试验结果表明,热风烧结可以提高钒钛磁铁精矿烧结矿的成品率和转鼓强度,但利用系数降低;
The test results show that hot- air sintering can increase sinter rate and tumbler strength, but decrease productivity.
烧结矿矿相分析发现,即使用较粗焦粉的试验需要的燃料消耗率更低,但烧结成品包含的磁铁矿相更多,再生赤铁矿的含量更少。
Sinter mineralogical analysis found that even though tests with coarser coke required lower fuel rates, the product sinters contained more magnetite phase and less secondary hematite.
在高碱度条件下,运用正交组合分析手段,对钒钛磁铁精矿的烧结工艺进行烧结实验研究分析。
Using analysis methods of orthogonal combination under the conditions of high alkalinity, sintering process on Vanadic Titanomagnetite are researched.
永磁铁气体各种开头标准尺寸是指烧结后,经磨削或绕结后直接为成品的符合客户要求的标准尺寸。
The standard sizes of all hard ferrite magnet shapes mean the Ones of finished products which undergo sintering and grinding processes.
在新的配矿条件下,研究了碱度对承钢钒钛磁铁烧结矿的强度、矿物结构和烧结过程的影响。
The influence of sinter basicity on quality, mineral structure and sintering process of vanadium-titanium magnetite was determined under the new raw material structure.
特别适用于锰锌高导软磁铁氧体和低功耗软磁铁氧体等高档铁氧体材料的气氛烧结。
It is especially applicable for sintering Mn-Zn soft ferrite material with high permeability and low power loss.
介绍了我国软磁铁氧体烧结氮窑用推板的生产使用情况,讨论了实现软磁铁氧体烧结氮窑用推板国产化亟待解决的关键问题。
Present status of push slab for sintering soft-magnetic ferrites in nitrogen kiln are introduced in this paper. In addition the key problems to be resolved for producing push slab were discussed.
针对攀钢钒钛磁铁精矿品位提高的情况,在实验室进行了高品位攀精矿烧结试验研究。
Pointed to the case that the grade of Panzhihua concentrates was increased, the laboratory test with high grade concentrates was conducted.
针对攀钢钒钛磁铁精矿品位提高的情况,在实验室进行了高品位攀精矿烧结试验研究。
Pointed to the case that the grade of Panzhihua concentrates was increased, the laboratory test with high grade concentrates was conducted.