研究了涂料层中不同耐火粉料及粘结剂等因素对涂层强度的影响。
Some factors affecting coating strength, such as refractory and binder, were studied.
胶乳在涂料中起到粘接颜料粒子及颜料与纸基的作用,增强涂层强度。
The main function of latex is to bond pigment particles, then to build up the film strength.
涂层强度决定了印刷时是否会产生大量纸粉,是决定印刷质量的重要指标。
B. coating strength determines whether the printing will produce large amounts of paper powder, it's very important in determining the quality of printing.
每片涡轮机叶片由高强度单晶合金制成,上面覆盖强韧陶瓷涂层。
Each blade is grown from a single crystal of alloy for strength and then coated with tough ceramics.
结果:术后每一时间段涂层植入体界面抗剪强度均显著高于非涂层者。
Result: Isogradient HA-coated implants had a greater average interface shear strength than the uncoated ones at each time span.
结果:在术后任一时间段涂层植入体界面抗剪强度均显著高于非涂层者。
Result: Isogradient ha coated implants had significantly greater average interface shear strength than the uncoated implants at each of the time interval.
在具有更为复杂的预成形几何形状的适当基体上将聚晶半刚石用作高强度薄涂层表面材料应当说是很容易的事情。
Applying polycrystalline ballas diamond as material for high-duty, thin coating surfaces on suitable substrates with even complex pre-shaped geometries should be quite easy.
通常,涂层纸的墨粉定影强度较低且制卡质量低。
Typically, coating paper Toner low emolument and making quality and low.
测定了涂层抗拉强度、膨胀系数、一定条件下的磨损体积、气孔率等性能。
The properties of coatings. e. g. tensile strength, expansion coefficient, wear volume under given conditions and porosity, etc. were tested.
然后测量涂层和基体的硬度,并通过采用旋转弯曲疲劳试验比较涂层试样与未涂层试样的疲劳强度。
Then hardness of coatings and substrate was measured. By means of bend-rotation fatigue tests, fatigue strength of coating and uncoating specimens was compared after hardening and tempering.
结果表明,散射强度与表面纹理结构、涂层材料的光学性质有关。
The results indicate that scatter intensity is dependent on surface veins and optical properties of coatings.
这套模具在测量火焰喷涂聚合物涂层自拉伸强度方面实用、快速、简单。
The mould is useful, rapid and simple in measuring the self tensile strength of flame spraying polymer coatings.
涂层的抗拉结合强度与耐磨性之间存在着正比关系。
The wear resistance was directly proportional to the tensile strength of the coating.
试验结果表明:涂层刀片干铣削高强度钢的加工性能优异,工件加工表面质量达到半精磨水平。
The advantages of coated cemented carbide tool in dry milling of high-strength steel are demonstrated, and the workpiece surface roughness reaches the level of semi-finishing grinding.
在碳钢表面制备了具有梯度结构的PPS/FEP复合防腐蚀涂层,采用拉开法测定了各涂层体系的结合强度。
The gradient PPS/FEP composite anti-corrosive coatings were prepared on carbon steel. The bonding strength of all coating systems was determined by the pull-off test.
结果表明,增塑剂含量增加、增塑效率提高使涂层织物撕裂强度降低。
The results indicate that tearing strength of coated fabric decreases with the increase of the plasticizer concentration and plasticizing efficiency.
涂层与骨组织之间的结合强度用推出实验进行测量。
The bond strength between bone and titanium coatings was also measured by push-out test.
火焰喷涂具有设备简单、使用方便、操作成本低的特点,但它的涂层结合强度低,气孔率及氧化物含量高。
Flame spray possesses the characteristics of simple equipment, easy of use and low operating cost, but the coating adhesive strength is low, and porosity and oxidation is high.
通过玻璃纤维增强塑料的车削试验,研究了薄膜与基体之间的附着强度、涂层刀具的磨损和加工工件的表面粗糙度。
The adhesive strength of the films to the substrates, diamond-coated tool wear and surface roughness of the workpiece were further studied by turning glass fiber reinforced plastic cylindrical bars.
并且针对热扩散对涂层的结合强度及组织的影响分别进行了论述。
The effect of the hot diffusion on the bonding strength and the microstructure of the coating was individual discussed.
涂层与基体的剪切结合强度是评定涂层质量的重要指标,也是进行制造工艺优化的依据和基础。
Adherent strength of shearing is an important criterion in evaluating the quality of coating layers, and it is also the foundation to optimize manufacturing.
热喷涂层与基体的结合强度是衡量涂层质量的重要指标。
The bond strength of thermal sprayed coating is an important part for evaluating the quality of coating.
界面压入法适合于评价高结合强度的涂层。
This interfacial indentation method is suitable for use in those coatings with high bonding strength.
以此测量了铁基涂层的结合强度,证明了方法的有效性。
The bond strength of an iron-base coating material was measured and the validity of the method was proved.
在试验的喷距范围内,喷距对粉末的熔化状态和涂层结合强度均无明显影响。
The melting state of powder and bonding strength of coating did not vary much within spraying distance in the experiment.
界面强度是薄膜涂层材料的最重要的性能指标之一,目前尚缺乏有效的测量方法。
Interface strength is one of the most important properties of coating materials. There are no effective evaluation methods yet.
对基布中不同比例涤纶变形丝涂层织物的剥离强度进行分析。
This paper analysed the influences of different proportion of the interlaced yarns in the fabrics on bonding strength.
研究了试验参数对涂层界面结合强度的影响以及阳极氧化状态参数对钛基体表面形貌的影响;
The effect of the experimental parameters on the interfacial bonding strength was investigated, as well as the influences of the anodic oxidation state on the titanium substrate surface appearance.
T8涂层中由于碳元素被大量烧损,导致涂层氧化严重,孔隙率高,这是造成涂层硬度和强度不高及耐磨性较差的主要原因。
The burning loss of carbon, which causes heavy oxidation and high porosity, is the main reason for lower hardness, strength and worse wear resistance of T8 coating.
T8涂层中由于碳元素被大量烧损,导致涂层氧化严重,孔隙率高,这是造成涂层硬度和强度不高及耐磨性较差的主要原因。
The burning loss of carbon, which causes heavy oxidation and high porosity, is the main reason for lower hardness, strength and worse wear resistance of T8 coating.