通过试验,研究了水玻璃模数及其掺量对碱矿渣水泥性能的影响。
Through experiment, the influence of glass water modules and its mixing rate to the alkali slag cement performance is studied.
研究结果表明,随着水玻璃模数的增加,无机矿物聚合物混凝土的收缩呈现先降低后增加的趋势;
The results show that shrinkage of concrete firstly decreases and then increases , with the increase of modulus of water glass.
通过混凝土收缩试验,研究了水玻璃掺量、水玻璃模数、液固比、胶凝材料用量等因素对无机矿物聚合物混凝土收缩性能的影响。
The effect of various factors shrinkage property of slag based geopolymer concrete are studied by shrinkage test, such as content and modulus of water glass, liquid-solid ratio, gel material content.
试验研究表明:(1)水玻璃在比重和模数分别为1.5和1.1时,对矿渣激发的效果最好。
The research indicate that (1) when the specific gravity and modulus of soluble glass is 1.5 and 1.1, the effect of activate slag is best.
本文提出了由稻壳灰制高模数的水玻璃和活性炭的新工艺。
A new way of preparing big modulus sodium silicate and active charcoal from rice dusk ash was described.
采用超低模数的钠水玻璃可以有效解决高纤维素焊条的碳化和压涂问题。
Using sodium water glass with super low mode, carbonization and press coating problems during manufacture can be solved.
使用较高模数的水玻璃混制的型砂具有残留强度低、吹CO2时间短等优点,并有好的抗吸湿性和表面稳定性。
The sodium silicate sand prepared with higher modulus sodium silicate has advantages of low residual strength, short CO2 blowing time, high moisture absorption ability and surface stability.
实验表明,低模数水玻璃对三种废渣的激发效果最好。
The test results showed that the activation effect of low-modulus water glass is optimal.
实验表明,低模数水玻璃对三种废渣的激发效果最好。
The test results showed that the activation effect of low-modulus water glass is optimal.