主要研究了气相法白炭黑和ZDMA之间的协同补强效应。
The synergistic reinforcement effect between fumed silica and ZDMA was investigated in detail.
当同时添加气相法白炭黑和ZDMA时，会观察到明显的协同补强效应。
The obviously synergistic reinforcement of fumed silica and ZDMA to SBR was observed.
通过添加气相法白炭黑增加硅橡胶硬度，添加金属氧化物（二氧化铈）改善硅橡胶热稳定性。
The effects on the heat resistant properties of the metal oxides, such as ceria, ferric oxide and fumed titania etc, to the copolymerized fluorosilicone rubber SKTFT-25.
采用Z桨捏合机，将端乙烯基硅橡胶、气相法白炭黑及羟基硅氧烷进行混炼，制备了高强度硅橡胶混炼胶。
High strength silicone rubber compounds were prepared using vinyl-terminated silicone rubber, fumed silica and hydroxy siloxane by intensive mixing method in Z blade mixer.
介绍了气相法白炭黑输送过程的特点，常见的气固分离方法及分离设备的选择，扩散式旋风分离器的结构特点、参数选取等。
The common gas-solid separations and transportation equipment, as well as the structural features and parameters selection of the cyclone-proliferation separator were summarized.
此产品比表面积高、细度小，能替代气相法白炭黑用于硅酮胶与胶粘剂行业，用作透明填充补强剂，使产品取得很好的使用效果。
Small fineness, can substitute vapor-phase white carbon black in silicon ketone glue and adhesives industries, as transparent reinforcing agent for application effect.
试验结果表明，加入湿法白炭黑超细粉的试样拉伸强度比添加气相法白炭黑者提高了54%，扯断伸长率提高了64%，磨耗量降低了20%。
The results showed that the sample by adding the ultrafine powders of silica aerogel increased the tensile strength 54%, the elongation at break 64%, decreased the abrasion loss 20%.
本文系统地描述了白炭黑在工业中的应用，并介绍了现有的白炭黑制备方法，如以蒙脱石为原料的碱浸法、以四氯化硅为原料的气相法、以水玻璃为原料的沉淀法等。
The authors introduce its application in many fields and its current preparation techniques, e. g. taking montmorillonite as raw material to prepare amorphous silica by NaOH liquor lixiviation;
本文系统地描述了白炭黑在工业中的应用，并介绍了现有的白炭黑制备方法，如以蒙脱石为原料的碱浸法、以四氯化硅为原料的气相法、以水玻璃为原料的沉淀法等。
The authors introduce its application in many fields and its current preparation techniques, e. g. taking montmorillonite as raw material to prepare amorphous silica by NaOH liquor lixiviation;