以及焊缝横向、纵向收缩对底架定位的影响。
The impacts of transverse and longitudinal shrinkage of welding seam on underframe positioning.
利用弹性理论。给出了薄壁圆筒纵向焊缝的横向收缩引起的应力与变形的定量解答。
According to elastic theory, this paper gives quantitative answers of stresses and deformations caused by the lateral contraction of longitudinal welding seam on the thin wall's cylinder.
通过严格控制原料的夹杂物级别和优化焊接、定径工艺可以有效地消除焊缝横向裂纹的产生。
It is efficient to eliminate the occurrence of transverse crack on weld by means of optimizing welding, sizing process and strictly control to inclusions class of raw material.
X65管线钢在焊接过程中,内侧焊缝金属出现横向和纵向沿熔合线方向的裂纹,横向裂纹贯穿焊缝金属横截面。
The longitudinal cracks along bond line and the transverse cracks which cut across the weld metal cross section inside weld metal were formed, while X65 pipe line steel was welding.
添粉和不添粉的5A02和5A06铝合金拼焊板的横向拉伸试件均断裂于薄板母材,证明焊缝的强度合格。
The longitudinal tension PM specimen of Tailor Welded Blanks of 5A02 and 5A06 were all fractured on the thinner base metal, which indicated that welds were eligibility.
前轮对处于脆性温度区间的焊缝金属施加一个横向挤压塑性应变,减小甚至抵消致裂的拉伸应变,防止了焊接热裂纹的产生。
The front impact roller causes transverse plastic compression strain in the weld which is in the brittle temperature range, which counteracts the tensile strain which leads to hot cracking.
横向收缩变形:构件焊后在垂直焊缝方向上发生的收缩。
Transverse/cross/lateral contraction deformation:The component contracts in the upright direction of weld after weiding.
结果表明,通过外加横向磁场对熔池进行搅拌,可以使焊缝晶粒得到细化,进而使其抗拉强度和硬度等力学性能得到改善;
The results show that transverse magnetic field can refine the primary crystallization structure by electromagnetic stirring and improve the ultimate strength and hardness of the welded joint.
研究了外加横向电流对铝合金CO_2激光焊接焊缝成型的影响。
The influence of transverse current on seam formation of CO2 laser beam welding of Aluminum alloys has been investigated.
后轮将焊缝金属的纵、横向压缩塑性变形充分碾展,减小了工件的残余变形和应力。
The rear impact roller stretches the weld longitudinally with transverse compressive plastic deformation of the weld, thus reducing the residual deformation and stresses in the bead.
在焊缝附近的横向残余应力既有拉应力,也有压应力;
In the weld transverse residual stress near the tensile stress, also had both compressive stress;
在焊缝附近的横向残余应力既有拉应力,也有压应力;
In the weld transverse residual stress near the tensile stress, also had both compressive stress;