本文研究了具有不同晶格取向的铜的氧化特性。
The influences of crystal orientation on copper oxidation were investigated.
多晶生长暂停拉伸时,新晶粒将在柱状晶顶部晶界夹角处形核并长大,而且新晶粒的晶格取向与原有晶粒的取向无关。
When pulling halts, the combination of grains occurs, and the lattice orientation of new grain is not related to the original grains.
合金碳化物晶格常数的变化未导致新的取向关系。
The change in lattice parameter of secondary carbides caused by high alloying does not result in any new orientation relationship.
发现冲击波的主要效应体现为对晶粒的破碎、细化和取向作用,对晶格结构几乎没有影响。
It is found that shock wave mainly changes the crystallite size and orientation, but has little effect on its lattice structure.
同时发现衬底晶格是否匹配与C_(60)取向膜的生长关系不大,而具有弱表面键的衬底有利于C_(60)膜的取向生长。
Moreover, the substrate with weak surface dangling bands was found to be necessary for the oriented growth of C60 films.
结果表明,波导层内含有均匀分布的三维应变场,晶格常数的变化随着波导取向的不同而呈现各向异性特点。
It is found that the waveguide layer contains uniformly distributed three dimensional strains and the variation of lattice constants in the waveguide depends closely on the waveguide orientation.
结果表明,波导层内含有均匀分布的三维应变场,晶格常数的变化随着波导取向的不同而呈现各向异性特点。
It is found that the waveguide layer contains uniformly distributed three dimensional strains and the variation of lattice constants in the waveguide depends closely on the waveguide orientation.