结果表明在接枝度为15%、高岭土填充量为10%时，体系具有较高的拉伸强度。
The results showed when the grafting degree was 15% and kaolin content was 10% , the blend system had a better tensile strength.
聚丙烯凝胶电泳(SDS - PAGE)分析结果表明，随着接枝度(DG)的增加，接枝物的亚基谱带逐渐减少，糖基谱带变得明显。
According to the analysis of SDS-PAGE, the bands of the graft subunits decreased and the glycosyl bands were seen more clearly with the degree of graft (DG) increasing.
射线衍射测试表明，接枝膜结晶度随接枝率的升高而降低。
X-ray test found that the grafted membranes show a decrease in crystallinity depending on the grafting yield.
接枝后家蚕丝的白度和染色性略有下降，染色色牢度与未处理真丝织物基本相同。
The whiteness and dyeability of the grafted silk fibers were slightly decreased, and the dye fastness remained basically similar to that of the ungrafted fibers.
接枝物的结晶峰温、熔融峰温、结晶度及结晶速度均低于纯pp。
The crystallization peaks, melt temperatures, crystallinity and crystallization rates of the grafted PP are lower compared to pure PP.
本文采用高取代度季铵型阳离子淀粉、氨基烯烃聚合物以及紫外线吸收剂BP - 4接枝氨基烯烃聚合物作为阳离子化试剂对棉纤维进行物理改性，用于活性染料无盐竭染。
Cationic starch of quaternary ammonium type with high DS, polyamines and polyamines grafted with UV-absorber BP-4 were applied as cationic agents of cotton in salt-free dyeing of reactive dyes.
两步法在接枝率、交联度、管材成型速度和物料存放时间方面优于一步法。
The graft ratio, degree of crosslinking, processing rate of pipe and storage life of silane crosslinked PE product were better than those of the product by one-step process.
结果表明，氨等离子处理会对膜表面产生一定的刻蚀作用，从而影响膜表面的粗糙度及氨基接枝密度；
The results showed that plasma treatment would etch film surface, which would affect the roughness of film surface and the density of grafted ammonia group.
本文较详细地介绍了表层低交联度聚苯乙烯树脂及接枝聚苯乙烯树脂的制备过程及它们的一些物理性质。
The preparation of thin layer polystyrene resin and grafted polystyrene resin as well as their physical properties have been described in detail.
本文较详细地介绍了表层代交联度聚苯乙烯树脂及接枝聚苯乙烯树脂的制备过程及它们的一些物理性质。
The preparation of thin layer polystyrene resin and grafted polystyrene resin aswell as their physical properties have been described in detail.
射线衍射谱图显示接枝后亚麻纤维的结晶度下降。
X-ray diffraction spectrums show that the crystal degree of grafted flax has turned smaller than general flax.
射线衍射谱图显示接枝后亚麻纤维的结晶度下降。
X-ray diffraction spectrums show that the crystal degree of grafted flax has turned smaller than general flax.