探讨了新型接枝剂CY-1在全棉筒子纱无粉尘染色工艺中的应用；
Application of new type grafting agent CY-1 to non-dusting cotton package dyeing was re_searched.
考查了反应温度、引发剂用量、反应时间和胶用量对接枝共聚反应的影响。
The influence of reaction temperature, initiator level. reaction time and rubber level on the graft polymerization was investigated.
研究了单体浓度、引发剂浓度、反应时间和反应温度对接枝聚合物接枝率、凝胶率等的影响。
The influences of concentration of BPO, concentration of monomer, reaction time, reaction temperature were investigated in terms of grafting degree and gel content.
在明胶上接枝丙烯酸丁酯是以硝酸铈铵为引发剂在水介质中进行的。
The grafting of butyl acrylate (BA) onto gelatin, using ceric ammonium nitrate (CAN) as redox initiator in aqueous medium, has been studied.
介绍了利用淀粉为基材，接枝丙烯酰胺制备环保型高分子絮凝剂的方法。
The green polymeric flocculant is prepared by starch grafting acrylamide in the research.
本论文第一部分是关于制备优异抗冲接枝共聚物的新工艺和方法，其抗冲接枝共聚物可以单独用做改性剂使用或者和热塑性树脂形成混合物使用。
Part one in This paper relates to a novel process for producing an excellent impact resistant graft copolymer which can be used in itself alone or in the form of a mixture with a thermoplastic resin.
研究了膜在光引发剂溶液中的浸泡时间、单体溶液的浓度、反应温度和紫外光照射时间等对接枝效果的影响。
Influences of immersion time of film in the solution of initiator, monomer concentration, reaction temperature and UV irradiation time on grafting effect are studied.
研究了单体质量分数、引发剂质量分数、反应温度和转子转速对接枝聚合物接枝率的影响。
The influences of monomer mass fraction, DCP mass fraction, reaction temperature and rotating velocity on grafting degree were investigated.
阐明了聚乙烯毛细管辐射接枝苯乙烯时，剂量、剂量率、单体浓度、溶剂、温度和交联剂等对接枝率的影响。
The effects of dose, dose rate, monomer concentration, solvents, temperature and crosslinking agents on the graft copolymerization of styrene with polyethylene capillary were illustrated.
以棉纱和粘胶丝为试料，研究了利用硝酸铵铈为引发剂的纤维素与丙烯腈的接枝共聚。
The graft copolymerization of acrylonitrile onto cotton yarn and viscose rayon with ceric. ammonium nitrate as initiator has been studied.
对臭氧活化时间、接枝单体用量、水性抗静电剂的浓度等条件进行了优化。
The ozone activation time, the content of hydrophilic monomer and the concentration of antistatic agent were optimized.
此外还研究了单体浓度、反应温度、添加剂等因素对接枝率的影响。
Effects of factors on grafting rate were investigated, such as monomers concentration, reaction temperature, additives and so on.
考察了单体浓度、发剂浓度、合温度对接枝共聚反应的影响。
Effeets of monomer concentration and reaction time on the graft copolymerization were studied.
研究了以过氧化苯甲酰（BPO）为引发剂、甲苯为溶剂的SBS接枝丙烯酸酯共聚反应。
The grafting-copolymerization of acrylate to SBS block copolymer in toluene solution with BPO as initiator was studied.
研究了以硝酸铈铵、过硫酸铵、过硫酸铵-亚硫酸氢钠为引发剂玉米淀粉与丙烯酸的接枝共聚反应。
Graft polymerization of acrylic acid onto maize starch using ceric ammonium nitrate, ammonium persulfate and ammonium persulfate sodium bisulfate as initiators is studied.
研究了纤维的预辐照剂量、单体浓度、摩尔盐含量、交联剂含量以及接枝温度和时间等条件对接枝共聚反应的影响。
The effects of pre irradiation dose, monomer, Mohr's salt and crosslinking agent concentration, grafting temperature and reaction time on grating copolymerization were investigated.
以硅烷偶联剂KH550为桥梁，利用酰胺化反应将改性的HBPE(记做MHBPE)接枝到超细二氧化钛表面。
By use of silane coupling agent KH550 the modified HBPE (MHBPE) was grafted onto the surface of ultrafine titanium dioxide by amidation reaction.
研究了马来酸酐接枝天然橡胶(MNR)作为改性剂，对废报纸粉(PF)填充聚氯乙烯(PVC)复合材料的力学性能和热学性能的影响。
Maleic anhydride grafted natural rubber (MNR) was used as modifier, and its effect on the mechanical properties and thermal property of waste newspaper flour (PF) filled PVC composites was studied.
以混凝土外加剂分子设计原理为指导，以绿色化学为基础，研究了新型接枝聚合物保坍剂的绿色合成工艺。
Based on green chemistry and molecular design theory of concrete admixture, the cleaner synthesis of novel grafted polymeric concrete slump retaining agent has been studied.
用阳离子淀粉接枝窄相对分子质量阴离子聚丙烯酰胺制备干增强剂。
The graft copolymer of cationic starch and APAM with narrow molecular weight distribution was prepared and used for dry-strengthening agent.
用正交法探讨了以高锰酸钾为引发剂的竹纤维与丙烯酸接枝共聚改性反应。
An orthogonal method is used to study the grafting copolymerization of bamboo fiber with acrylic acid by using potassium permanganate as an initiator.
以二叔丁基过氧化物(DTBP)为引发剂，在反应型双螺杆挤出机中进行ABS接枝马来酸酐的研究。
It was studied that ABS was grafted by MAH, using DTBP as initiator, and reacted in twin-screw extruder.
以硝酸铈铵为引发剂将丙烯酸丁酯(BA)与淀粉(s)接枝共聚，考察了淀粉糊化对接枝反应的影响。
Graft copolymerizations of butyl acrylate (BA) onto starch (s) were carried out with ceric ammonium nitrate as initiator, and influence of starch pasting on graft reaction is tested.
研究了CR/SBS/MMA接枝胶黏剂的配方和工艺条件对其剥离力的影响。
The influences of composition and synthetic conditions on stripping strength of CR/SBS/MMA graft adhesive were investigated.
本文研究了引发剂浓度、反应温度及反应时间对表观接枝率(g_a)和抗收缩系数(ase)值的影响。
In this paper, the concentration of initiators, reaction temperature, reaction time and their effects on apparent grafting efficiency (G_a) and anti-shrinkage efficiency (ASE) value have been studied.
总结了近年来淀粉与乙烯基单体接枝共聚的常用引发剂，对引发剂的性质、优缺点、引发机理及应用作了评述，引用最新文献21篇。
Normal initiators used for graft polymerization of vinyl monomers on starch are reviewed with 21 references. The characterization, initiating mechanism and the application of initiators are discussed.
本发明涉及菜籽油接枝共聚加脂剂的制备方法。
This invention relates to a method for preparing colza-oil-grafted copolymerized fatting agent.
单体质量分数、引发剂质量分数增加，接枝率增加。
The grafting degree increased with the increase of monomer mass fraction and DCP mass fraction.
用硝酸铈铵作引发剂，研究了淀粉丙烯酰胺接枝共聚物高分子絮凝剂制备的工艺条件。
The process condition of preparation of polymeric flocculant of graft copolymer of acrylamide onto starch by using ceric ammonium nitrate as initiator are studied in this article.
用硝酸铈铵作引发剂，研究了淀粉丙烯酰胺接枝共聚物高分子絮凝剂制备的工艺条件。
The process condition of preparation of polymeric flocculant of graft copolymer of acrylamide onto starch by using ceric ammonium nitrate as initiator are studied in this article.