沿着晶界发生的应力腐蚀开裂。
Stress corrosion cracking in which the cracking occurs along grain boundaries.
空心圆柱滚子轴承为应力腐蚀磨损失效。
The failure of the hollow cylinder roller bearing is stress corrosion wearing.
为了防止应力腐蚀需要进行除应力处理。
Stress relief treatment is necessary to prevent stress corrosion.
本文首先阐述了研究轨钢应力腐蚀的意义。
The significance of stress corrosion test for rail steel is demonstrated.
研究了亚稳态奥氏体不锈钢的应力腐蚀开裂。
The stress corrosion cracking of metastable austenitic stainless steel has been investigated.
应力腐蚀破裂机制为膜破裂控制的阳极溶解。
The mechanism of SCC is an anodic dissolution with film rupture rate-controlling.
应力腐蚀试验研究。
本文研究了带裂纹混凝土梁的应力腐蚀断裂问题。
Stress corrosion cracking problem of concrete beams with crack is studied in this paper.
文中还对氢脆在应力腐蚀开裂中的作用进行了讨论。
The role of hydrogen embrittlement in stress corrosion cracking has also been discussed.
进行了模拟原电池试验和预蠕变试样的应力腐蚀试验。
Simulated galvanic cell tests and stress corrosion tests using pre-creeping specimens were conducted.
硫化物应力腐蚀是引起输气管道失效的主要原因之一。
The sulfide stress cracking is one of the reasons of gas transmission pipeline failure.
分析结果表明,高压油管的开裂是应力腐蚀开裂造成的。
The results show that the cracking of the pipe is a kind of stress corrosion cracking.
结果表明,断裂失效的原因主要是应力腐蚀和腐蚀疲劳。
The results show that stress corrosion and corrosion fatigue are the main causes for the fracture failure.
结果表明,该进气管断裂系由于应力腐蚀裂纹失稳扩展所造成。
The results show that the failure of the tube is due to stress corrosion crack propagation.
应力集中可能会导致疲劳、应力腐蚀或氢基应力腐蚀而产生裂纹。
Stress concentrations can lead to initiation of cracking by fatigue, stress corrosion, or hydrogen-assisted stress corrosion.
还会形成穿透型裂纹,造成镀层下本体金属的疲劳或应力腐蚀裂纹。
Through-thickness cracking also can lead to fatigue or stress corrosion cracking of the base metal beneath the plating.
还有反应堆冷却剂系统焊接问题,它们使用了并且得到原生水,应力腐蚀裂痕。
There are reactor coolant system weld issues, they're used and they're getting primary water stress corrosion cracking.
在镀层存在缺陷时,镀金、镀镍层均促进柯伐合金的应力腐蚀开裂。
When the plating exist defect, the gold-plating nickel -plating both promote the stress - corrosion fracture of Kovar alloy.
结果表明,纤维取向对玻璃纤维增强塑料的应力腐蚀行为有很大影响。
The results show that the fibre orientation affects on the stress corrosion cracking of GRP seriously.
应力腐蚀开裂(SCC)是压力容器及管道腐蚀失效的主要形式之一。
SCC is one of the main forms of corrosion accidents of pressure vessels and pipes.
结果表明,波纹膨胀节发生早期失效是由于构件发生应力腐蚀开裂所致。
The results show that the early failure of the corrugation expansion joint was results from the stress corrosion cracking in the components.
固溶处理是改善和提高奥氏体不锈钢波纹管抗应力腐蚀能力的有效措施。
And solution treatment is the valid method to improve the anticorrosion property of the austenite stainless steel bellows.
复板焊接结构出现应力腐蚀开裂的主要原因之一是拉伸残余应力的作用。
One of main reason for producing SCC in cladding plate weldments is the role of tensile residual stresses.
由于这些气瓶盛装的介质常含有腐蚀性,易引发气瓶产生应力腐蚀等缺陷。
The gas cylinder is easy to be eroded or caused other disfigurement because of the erodible medium in it.
在对各项试验结果进行综合分析之后确认,该管路泄漏失效为应力腐蚀破坏。
After the integrated analysis of each test result, it is proved that the pipe leakage failure is of stress corrosion damage.
本文研究了不同的形变时效处理对LY 12铝合金应力腐蚀开裂性能的影响。
The effect of different deformation-aging treatments on the stress corrosion cracking of LY12 aluminum alloy was studied.
随后斑点穿过压缩层继续扩展,剩余应力发生改变,斑点最终导致应力腐蚀裂纹。
The pit then grows through the compressive layer, and the change in residual stress state and the pit geometry initiate stress corrosion cracking.
本文介绍了焊接残余应力对金属结构的静强度、脆性断裂以及应力腐蚀开裂的影响。
The paper discusses over the influence exerted by welding residual stress on the static strength, brittle fracture and stress-corrosion cracking of metal structure.
其原因是磁屏表面存在较大的切向拉应力,从而在酸洗过程中产生了应力腐蚀开裂。
The presence of the greater residual tensile stress induces the stress corrosion cracking in the course of the acid pickling.
其原因是磁屏表面存在较大的切向拉应力,从而在酸洗过程中产生了应力腐蚀开裂。
The presence of the greater residual tensile stress induces the stress corrosion cracking in the course of the acid pickling.