利用填充法直接制备宏孔的多孔玻璃载体颗粒。
Macro pore porous glass microorganism carrier beads were prepared by stuffing salts.
在所述无机多孔玻璃管外表面的至少一部分上设有无机晶状陶瓷涂层。
An inorganic crystalline ceramic coating is received on at least a portion of the inorganic amorphous glass tube exterior surface.
总结出了多孔玻璃微珠孔径的控制方法和提高多孔玻璃微珠的吸附量的有效方法。
At last, the effective means of control the aperture of porous glass microsphere as well as the means of increasing the adsorption amount of porous glass microsphere is proposed.
本文报告了以多孔玻璃为基材的微通道板的制备及其二次电子发射特性的测量结果。
The paper reports the fabrication of the MCP based on the porous glass (ceramics) and the measurement of secondary electron emission characteristic of the MCP.
对多孔玻璃微珠作为多孔性固体吸附剂的研制及其在液相中的吸附性能做了初步研究。
As a porous solid adsorbent, porous glass microspheres were prepared and its adsorption feature in liquid phase was investigated.
同样,悬臂式檐金属包钢结构和烧结多孔玻璃汇合而成的波浪也呈现着层层流动要素。
Similarly the cantilevered canopies of metal clad steel structure and fritted pattern glass merge the wave forms into a series of repeating flowing elements.
对于沿街立面的设计,是两个透明层包在多孔玻璃里,这打破了巨大的体量,呼应了人的步行尺度。
The street fa? Ade, which consists of two transparent levels clad in patterned fritted glass, is set back, breaking up the overall mass and responding to the scale of pedestrians.
用光谱仪测定多孔玻璃的紫外可见近红外光谱,对光谱透过率与浸析效果之间的关系作了定性分析。
The relationship between the transmittance and leaching effect of the glasses was discussed by measuring UV VIS NIR spectrum.
通过对多孔玻璃微珠组分对比,分相温度、时间的对比,酸溶时间的对比,得到控制多孔玻璃微珠最佳工艺。
Through the comparison of ingredient, the phase separation temperature and time, acid treatment time, we get the best technology of how to control the aperture of the porous glass microsphere.
分相玻璃在浸析过程中由于组成、分相制度、冷却速度的不同,而使多孔玻璃受到拉应力或压应力,通过改善浸析条件可制得具有一定强度、没有裂纹的多孔玻璃。
In the process of leaching, porous clad of phase separated glass may has tensile stress or compressive stress because of the different copmposition, phase separation condition and cooling rate.
采用有机泡沫浸渍法制备羟基磷灰石-生物玻璃多孔复相陶瓷。
The porous hydroxyapatite-bioglass duplex ceramic was prepared by the dipping method with polymer foam.
介绍了聚四氟乙烯分散液的概念和有关性能。叙述了PTFE玻璃布及其衍生产品和PTFE多孔金属的性能和用途,制备原理、方法和工艺。
Concept of PTFE dispersion and its performance are introduced. PTFE glass cloth, its derivative products and PTFE porous metal, preparation thesis and method process are reviewed, respectively.
叙述了PTFE玻璃布及其衍生产品和PTFE多孔金属的性能和用途,制备原理、方法和工艺。
PTFE glass cloth, its derivative products and PTFE porous metal, preparation thesis and method process are reviewed, respectively.
尝试采用添加造孔剂的方法制备了多孔生物玻璃材料。
Porous bioglass material was prepared by attempting to add pore former .
利用锂钙硼玻璃在磷酸盐溶液中的原位转化反应制备表面多孔的中空羟基磷灰石(HAP)微球。
Hollow hydroxyapatite (HAP) microspheres with pores on their surfaces were prepared by in situ conversion reaction of Li-Ca-B glass in phosphate solution.
注射管的末端提供有分散装置例如多孔塞或烧结玻璃。
The end of the injection tube is provided with a dispersion device such as a porous plug or fritted glass.
在适量的固相含量和生物玻璃的含量下,可制得孔结构满足骨组织工程支架材料要求的多孔陶瓷。
Porous ceramic with a pore structure meeting the requirements for the scaffold of bone tissue engineering could be prepared at suitable solid content and solid ratio.
在室内实验中,用玻璃器皿等不能准确反映泡沫在岩心多孔介质中的稳定性,为此研究了泡沫在均质岩心中的泡沫封堵的有效期。
Some inaccuracy often exists in the evaluation of foam stability in porous media using glass vessel in laboratory experiment, so the validity time of foam plugging in homogeneous core was researched.
本文报道利用二氧化硅微粒胶体溶液在玻璃和KDP晶体基质上制备多孔二氧化硅薄膜。
We report herein about the investigation on porous silica coatings prepared from colloidal silica solution on optical glasses and KDP crystal substrates.
离心玻璃棉属于多孔吸声材料,具有良好的吸声性能。
Centrifugal glass cotton belongs to the porous sound-absorbing material, have good sound-absorbing performance.
结果表明:玻璃屋入口流速对室内及多孔墙内空气的温度场与流场有较大的影响。
The result shows that the inlet velocity has significant influence on the temperature field and flow field in glass house.
采用毛玻璃模型、填充砂管和人造岩心封堵实验,研究了多孔介质的表面润湿性对交联聚合物溶液(LPS)封堵性能的影响。
The effect of surface wettability of porous media on the plugging properties of LPS was studied through the ground glass model, quartz sand-packed tube and artificial core plugging experiments.
通过将玻璃质物质支承在远离洗提液的多孔薄膜上来克服这些问题。
These problems have been obviated by supporting the glassy material on a porous membrane remote from the eluant.
计算结果表明,降低空气入口流速,可减小空气流动阻力,提高多孔墙的集热效率;附加玻璃通道的太阳能多孔墙可减小长波辐射损失,并且具有收集热空气的作用。
Results show that the flow resistance will be decreased and the collection efficiency of the porous solar wall will be increased with a decrease in the inlet air velocity.
结果表明:随着多孔二氧化硅孔面积的增加,层合玻璃中无机玻璃/聚氨酯界面的剪切强度先迅速增大后缓慢降低;
The results indicate that with the increasing of pore area, the shear strength between inorganic glass and polyurethane in laminated glass first increases rapidly, and then decreases slowly.
目的对生物玻璃BG 2 0多孔支架进行细胞相容性研究。
Objective to evaluate the cytotoxicity of a novel porous bioglass BG-20 as scaffolds.
SEM分析表明,提铝残渣颗粒形貌完全不同于粉煤灰原灰形貌,且多为不规则玻璃体颗粒,表面粗糙不平、并呈多孔、疏松结构。
SEM analysis show that morphology of the residue was mostly anomalistic vitreous body that the surface was coarse, poriferous and of lax structure, and therefore it was different from fly ash.
报道了玻璃-云母多孔材料研制的结果,研究了该材料的岩相结构,对材料的抗压强度、显气孔率、体积密度进行了测试。
The investigations were conducted experimentally on not only its petrogrphic structure but alsothe properties of its compressive strength, apparent porosity, apparent density and moisture content.
报道了玻璃-云母多孔材料研制的结果,研究了该材料的岩相结构,对材料的抗压强度、显气孔率、体积密度进行了测试。
The investigations were conducted experimentally on not only its petrogrphic structure but alsothe properties of its compressive strength, apparent porosity, apparent density and moisture content.