可将铝合金铸件加热到固溶温度。
An aluminum alloy casting can be heated to the solutionizing temperature.
晶粒生长指数随固溶温度的升高而增加。
Grain growth exponent increases with the increasing of solid solution treatment temperature.
本文研究了固溶温度对硬铝LY11组织与性能的影响。
The effect of solid solution temperature on the structure properties of LY11 aluminium alloy is studied.
重要的是较低的锻造温度和热处理固溶温度比较高的好得多。
It is important to control the forging temperature and solution treatment temperature lower rather than higher.
试验表明,不同固溶温度处理,LF6钢的层状析出量不同;
The results show that different solid solution heatreatment temperature results in amounts differences of separation.
但随固溶温度的升高,时效后复合材料的硬度的提高幅度有下降趋势。
In addition, the hardness of the composite after aging decreases with the increase of solution temperature.
实验表明,随着固溶温度的升高和固溶时间的延长,合金的相变点升高。
The experimental results indicated that with higher betatizing temperatures and longer betatizing duration, phase transformation temperatures of the alloys became higher.
可使铝合金铸件从固溶温度直接快速冷却到时效温度,省去了常规工艺的室温保持。
The aluminum alloy casting can be rapidly cooled from the solutionizing temperature directly to the aging temperature, eliminating the room temperature hold of a conventional process.
随固溶温度升高和固溶时间的延长,第二相颗粒回溶较多,但会发生再结晶,晶粒发生长大。
The secondary phase particle dissolves back more with the increase of solution temperature and holding time, but recrystallization will occur, grains grow up.
当挤压比一定时,随着在线固溶温度与时效温度的升高,线材的力学性能下降,导电性能升高。
For a given extrusion ratio, mechanical properties of alloy wire decrease and conductivity increases with increase of on-line solution temperature and ageing temperature.
采用适当固溶温度处理,该二合金晶粒度适中,可获得强度、塑性和抗热疲劳性能较好的配合。
By proper solution treatment the grain size of alloys was moderate, thus a good combination of strength, plasticity and the resistance to thermal fatigue was obtained.
叙述了标准热处理固溶加热温度与精化模锻件组织和性能的关系。
The relationship between solution temperature under standard heat treatment with the structure and properties of precision die forgings, was also presented.
介绍了固溶处理温度、淬火到时效间隔时间及时效制度等对2A70铝合金预拉伸厚板组织和性能的影响;
The effect of quenching temperature, the interval time from quenching to aging and aging institution to 2A70 aluminium alloy pre-stretching plate structure and properties are introduced.
研究了锰的质量分数、固溶处理温度和淬火冷却速度对锰不平衡偏聚的影响和不形成锰偏聚的条件。
It includes the effect of manganese content, solution treatment temperature and cooling rate on the non equilibrium segregation of manganese and condition of segregation formation.
文章利用自行开发的固溶物沉积激光测试系统,测试了凝析气平衡油在不同压力下的析蜡温度。
Using the laser testing system of soluble solid deposition developed by themselves, the wax-condensing temperature of equilibrium oil of condensate gas is tested under different pressure.
固溶处理温度对抗拉强度和延伸率有较大的影响。
Solution treatment temperature has a significant impact on the tensile strength and elongation.
应用取向分布函数(odf)研究了3104铝合金经不同温度固溶及时效处理后的冷轧织构组态。
The cold rolling textures of 3104 aluminium alloys after solution and aging were studied by means of orientation distribution functions (ODFs).
固溶处理温度的高低不仅影响第二相在基体中的溶解程度,还影响合金的回复再结晶过程进行的程度。
The temperature of solid solution treatment affected not only the degree of the second phase dissolved in the matrix alloy, but also the recovery and recrystallization processing level of the alloy.
装置具有温度采集、加热时间准确、及时冷却等优点,为不锈钢u形管固溶处理提供了自动化水平比较高的设备。
The device has these features that temperature acquisition, accurate heating time, timely cooling etc; it provides the high level automation device to steel U-tube solution treatment.
即叶轮断裂是由于锻造加热时温度控制不好导致过热,在随后的淬火工序中又因加热温度过低,组织固溶强化效果差等综合原因所致。
The results show that the wheel hub cracking during radial impact testing was caused by excessive content of magnesium in the alloy as well as the overheating of the alloy during the solution process.
观察其显微组织和晶粒度,测定其显微硬度,分析了金相组织、晶粒度和硬度随固溶退火温度、保温时间、冷却速度的变化。
The microstructure was observed and the grain size and Vickers hardness were measured, the changes of microstructure, grain size, hardness and solid solution annealing process were discussed.
观察其显微组织和晶粒度,测定其显微硬度,分析了金相组织、晶粒度和硬度随固溶退火温度、保温时间、冷却速度的变化。
The microstructure was observed and the grain size and Vickers hardness were measured, the changes of microstructure, grain size, hardness and solid solution annealing process were discussed.