奥里油中含钒量较多,是锅炉预防高温腐蚀设计中的大难题。
The large amount of vanadium in Orimulsion may cause unexpected problems in the prevention of high-temperature corrosion of furnace.
由三种不同成分的拉伸试验结果与金相组织可知:一组成分的含钒量增加,晶粒细化,从而强度增大。
The testing results and their microstructure show that the one with a higher vanadium content and smaller crystal grain has a high strength.
超细VC弥散分布于铁素体基体,随球铁含钒量增加,超细v C量趋于饱和,这部分碳化物在球铁的强化中起主要作用。
A saturated dispersion with ultrafine VC particles may be approached as the increasing of V content in the iron. This seems to play an important role in the prec...
超细VC弥散分布于铁素体基体,随球铁含钒量增加,超细v C量趋于饱和,这部分碳化物在球铁的强化中起主要作用。
A saturated dispersion with ultrafine VC particles may be approached as the increasing of V content in the iron. This seems to play an important role in the precipitation strengthening for fe...
含碳量达到2.3%后,基体以马氏体为主,耐磨性比低碳的高钒高速钢大幅提高。
After the carbon content reached 2.3%, the matrix is martensite primarily and the impact wear resistance performance enhanced largely compared with the low-carbon high vanadium high-speed steel.
本发明具有反应温度低、反应时间短、工艺简单、生产成本低等特点,更适合于工业上大批量生产,本发明制备的氮化钒合金含氮量高,更适合于钢铁工业炼钢要求。
The process has the features of low reaction temperature, short reaction period, low cost, etc, and the prepared vanadium nitride alloy with high nitrogen content is suitable for use in steel making.
实验结果表明:配碳量为26%及以上时,还原后有剩余的含碳物质存在,钒钛磁铁矿的还原效果好。
The experimental results indicate that there is surplus of carbon and the reduction is better when the addition of carbon is above 26%.
实验结果表明:配碳量为26%及以上时,还原后有剩余的含碳物质存在,钒钛磁铁矿的还原效果好。
The experimental results indicate that there is surplus of carbon and the reduction is better when the addition of carbon is above 26%.