对引起涂层老化的主要因素及加速老化试验设计原则进行了介绍。
In this paper, primary factors caused aging of organic coatings and principle of accelerated test design were introduced.
这批的存储方式在不同阶段的处理上有意的执行了一个加速老化试验。
The storage behavior of the lots, at different stages of processing, was studied by performing an accelerated aging test.
研究了加速老化试验对经不同装饰后的脲醛胶中纤板物理力学性能的影响。
This article studies the impact of the accelerated aging test to UF MDF decorated by different material about physical and mechanical properties.
通过加速老化试验和安定性测试,找出了改铵铜-3安全性变化规律及检测方法。
The stability trend and checking methods of GATo-3 propellant was given by the experiments of aged and invariability.
对西北地区生产使用的聚丙烯塑编袋进行了紫外线加速老化试验,并对结果进行了分析研究。
It carried out the ultraviolet accelerated aging test on the polypropylene woven sack produced and used in Northwest of China, and analyzed and studied the results.
对国产汽车所用210种涂层试样进行了湿热带大气环境自然曝晒试验及人工加速老化试验。
Natural exposing tests in humid tropics atmosphere environment and accelerated ageing tests for 210 coat test samples of domestic automotives are carried out.
阐述了美国QUV老化机和氙灯老化机在人工加速老化试验中的性能特点,以及各自的适用领域。
Characteristics of America QUV aging machine and Xenon lamp aging applied in artificial accelerated experiments are described. Their application fields are given also.
以聚丙烯长丝为对象,采用不同紫外线辐射强度的人工加速老化试验对其光氧老化过程进行研究。
The photo-oxidation ageing process of polypropylene filaments was studied by artificial accelerated ageing test using different intensities of UV irradiation.
通过加速老化试验,研究了HTPB/TD I/MAPO类聚氨酯材料的老化性能,探讨了其老化机理。
To investigate the main aging mechanism of HTPB/TDI/MAPO polyurethane material, the aging properties were studied by accelerating aging method.
本文分析了各种环境因素对高分子材料的影响,介绍了常用的几种加速老化试验的方法及老化材料防护措施。
The effect of environment factors on the ageing of polymer materials, the ways of artificial aging test and the ways of protection against ageing are introduced.
采用盐雾和紫外-冷凝室内人工加速老化循环试验的方法,对聚氨酯和丙烯酸两种典型的船壳涂料进行人工加速老化试验。
The degradation of two coatings systems based on polyurethane and acrylic were studied by exposed in UV-condensation chamber and salt-fog chamber alternately.
其中以粉煤灰50%、硅灰10%取代普通硅酸盐水泥的试验组,无论是试验室标准养护或是加速老化试验都表现出最优的耐久性。
Among which the experiment group using 50% fly ash, 10% silica fume instead of ordinary Portland cement shows rather better durability either in standard curing or the accelerated aging experiment.
文中讨论了橡胶制品的自然老化与加速老化的特点,介绍了固体火箭发动机用橡胶制品加速老化试验的方法和步骤,并给出了试验结果与结论。
In this paper, the characteristics of natural and accelerated aging of rubber product is discussed. Also, the method and procedure of accelerated ageing tests and the test results are presented.
通过海洋大气环境户外暴晒老化试验和盐雾加速老化试验,试验研究了不同硬段含量的聚天冬氨酸酯(PAE)聚脲涂层的耐海洋环境老化性能。
Polyurea coatings with different contents of hard segment polyaspartic ester(PAE) were investigated through aging tests of marine environment outdoor exposure and salt fog testing.
通过海洋大气环境户外暴晒老化试验和盐雾加速老化试验,试验研究了不同硬段含量的聚天冬氨酸酯(PAE)聚脲涂层的耐海洋环境老化性能。
Polyurea coatings with different contents of hard segment polyaspartic ester(PAE) were investigated through aging tests of marine environment outdoor exposure and salt fog testing.