摘要采取长时间浸水马歇尔试验和多循环冻融劈裂试验方法，对掺加了水泥、抗剥落剂的安山岩集料沥青混凝土水稳定性能进行研究。
Long term immersing Marshall test and frozen-thaw cycle test were used to investigate the anti-stripping performance of andesite asphalt mixture using cement and anti-stripping agent.
在本试验条件下，接触疲劳失效的主要形式为深层剥落和浅层剥落。
Under the condition of our experiments, the main forms of contact fatigue failure are deep-spalling and shallow - spalling.
片状剥落并没有打伤试验之后被看见。
采取长时间浸水马歇尔试验和多循环冻融劈裂试验方法，对掺加了水泥、抗剥落剂的安山岩集料沥青混凝土水稳定性能进行研究。
Long term immersing Marshall test and frozen-thaw cycle test were used to investigate the anti-stripping performance of andesite asphalt mixture using cement and anti-stripping agent.
试验过程中，柴油机各零部件均未发生断裂、剥落、烧蚀、粘结等异常现象。
During the experiment, the parts of diesel engine were not broken, peeled off, ablation or bonded.
试验结果表明，HVOF涂层经过15次整体热震试验后，涂层均保持完好无损，未出现裂纹及剥落等任何缺陷；
The test results showed that HVOF coating endured 15 times thermal shock was perfect without any defects, such as crack and spalling.
通过高温瞬时试验、剥落腐蚀试验、扫描电镜及力学性能试验，对经均匀化和不经均匀化的5083铝合金铸锭的轧制制品进行对比分析。
The rolling products by homogenizing ingot and non-homogenizing ingot are analysed and compared through high temperature property tests, corrosion tests, SEM analysis and machine property tests.
通过高温瞬时试验、剥落腐蚀试验、扫描电镜及力学性能试验，对经均匀化和不经均匀化的5083铝合金铸锭的轧制制品进行对比分析。
The rolling products by homogenizing ingot and non-homogenizing ingot are analysed and compared through high temperature property tests, corrosion tests, SEM analysis and machine property tests.