炼钢过程中用该产品堵住出钢口，倾倒钢液时自动脱落。
Use this product to plug up the steel-tapping hole in making steel, which will automatically fall off when dump the molten steel.
分析30t转炉出钢口损毁机理，找出寿命低的主要原因。
The main low life causes of tapping hole are found after analyzing damaged mechanism of tapping hole of 30t converter.
研究不同抗氧化剂搭配对镁碳质转炉出钢口管砖抗氧化性能的影响。
Effects of different anti-oxidants on the anti-oxidation properties of MgO-C tapping hole of a converter are studied.
超高功率电弧炉出钢口在使用过程中要经受钢液的冲刷、渣液的侵蚀、氧化和温度的剧烈变化。
The taphole of UHP-EAF should stand severe molten steel corrosion, slag erosion, oxidation and temperature change during operation.
介绍了镁炭质整体出钢口的损毁机理及生产工艺过程，对影响整体出钢口质量的工艺因素进行了分析和优化。
The wear mechanism and production process of monolithic magnesia-carbon tapping hole were presented, and the process factors affecting the quality of the tapping hole were analyzed and optimized.
试验表明，适当缩小出料口，处理量明显增加，而钢球消耗和负荷确明显减少和降低。
Experiments indicate that it can make the throughput increased clearly, and can make the ball consumption and load reduced clearly that the mill outlet is properly reduced.