如果表面共固化一层玻璃布，吸湿溶胀行为更加明显。
If a film of glasscloth was co-solidified on the GECM surface, the hygroscopic capacity was more remarkable.
共固化试验件损伤主要发生在筋条蒙皮连接界面，且填充区也发生破坏；
For co-curing specimens, failures happen at the interface of the skin and stiffener, and the core regions of the stringer also fail.
复合材料网格结构软模成型共固化工艺具有低成本，高效率和高质量的特点。
The soft-mold aided co-curing process of composite grids structures is an advanced techniques with the characters of low cost, high efficient and high quality.
研究结果表明：共固化方式下产生的残余应力要小于胶结共固化方式下的残余应力。
Results show that the residual stress in structure manufactured by co-cure method is smaller than that in structure manufactured by co-bonding methods.
结果表明，复合材料共固化过程中由于树脂渗透等原因，共固化复合材料的阻尼峰值仅为理想状态的54%左右且阻尼峰值所对应的温度向高温方向移动；
The results showed that the value of damping crest was 54% of the idealized one due to the interaction of the resin and the embedded viscoelastic material in the co-curing process;
[16]潘利剑，张博明，戴福洪。 简谐激励下共固化复合材料黏弹阻尼结构的损耗因子研究[J]。振动与冲击，2008，27（2）： 57-60。
PAN L J, ZHANG B M, DAI F H. Loss factor of viscoelastic damping composite material under harmonic excitation [J]. Journal of Vibration and Shock, 2008, 27(2): 57-60.
通过添加酚醛树脂二氯化锡固化剂可以获得性能更好的共混物。
A blend with better properties could be obtained by adding phenolic resin tin bichloride curative.
对于一些材料而言，如氧化物分散强化的合金或者定向固化的低共熔混合物，其使用似乎依赖于一个特殊的创始人或者创始人团队。
For some materials, such as oxide dispersion-strengthened alloys or directionally solidified eutectics, the usage seems to depend upon a particular author or group of authors.
采用双酚A环氧丙烯酸酯（EA）和聚氨酯丙烯酸酯（PUA）共混，加入活性稀释剂、光引发剂、颜料等制备了紫外光固化光纤涂料。
The UV curable coating of fiber ribbon was prepared by blending bisphenol A epoxy acrylate(EA) and polyurethane acrylate(PUA)and adding reactive diluent, photoinitiator and pigment.
由于在共混物中引入了芳香族氨酯键，增加了醇酸树脂漆膜的附着力、硬度、固化速度及表面能。
The introduction of polyurethane groups to the blend improved the adhesivity, hardness, curing speed and surface energy of alkyd resin.
合成了不饱和聚酯多元醇，进而采用化学共混法合成了室温固化的聚氨酯聚苯乙烯共混物。
The room temperature curing polyurethane-polystyrene blends were synthesized with a synthesized unsaturated polyester-polyol by chemical blending method.
合成了不饱和聚酯多元醇，进而采用化学共混法合成了室温固化的聚氨酯聚苯乙烯共混物。
The room temperature curing polyurethane-polystyrene blends were synthesized with a synthesized unsaturated polyester-polyol by chemical blending method.