为了使双相不锈钢具有满意的工程性能，在生产和加工制造过程中，应避免在易产生脆化的温度范围内长时间停留。
In order to obtain satisfactory engineering properties for the duplex stainless steels, long period stop at the embrittlement temperature range should be avoided during production and fabrication.
ADI水脆化是由于水分解的氢使adi基体组织中的应力诱变产生马氏体引起氢脆而导致的。
ADI water embrittlement was attributed to the decomposed hydrogen originated from water, resulting in hydrogen embrittlement of stress induced martensite in ADI matrix.
试样表面镀锡使ADI的抗拉强度和伸长率下降，镀锡层不能有效防止ADI的水脆化。
Soldering on ADI surface decreased the ADI tensile strength and elongation, and solder coating could not prevent from water embrittlement.
试样表面镀锡使ADI的抗拉强度和伸长率下降，镀锡层不能有效防止ADI的水脆化。
Soldering on ADI surface decreased the ADI tensile strength and elongation, and solder coating could not prevent from water embrittlement.