铸钢，青铜，铸铁和合金阀门。
后来又说2平炉电炉生产铸钢件。
Later added 2 open hearth furnaces for producing steel castings.
铸钢锁轴在加工螺纹时轴杆端头断裂。
Casting steel container rotating lock axle rod-head fracture in machining screw.
铸钢阀门锤击手轮，阀座环，楔形闸板。
分析讨论了钙处理对连铸钢浇注性能的影响。
This paper analyzes the influence of calcium treatment on the castability of continuous casting molten steel.
连铸钢水温度是连铸生产工艺的重要参数之一。
The molten steel temperature is one of important parameters of continuous casting process.
本文探讨了热变形高铬铸钢中颗粒状碳化物的形成。
This paper deals with the granular carbides formation from hot deformation in high chromium cast steel.
本文应用铸型涂料的理论研究了新的铸钢水基涂料。
The new water-based coating for cast steel was developed by using the theory of mould coating.
其中有的方法不仅适用于铸钢件，也适用非铁金属。
Some of these methods are applied not only to steel castings but also to nonferrous metals.
应采用低氢焊条焊接厚钢板与铸钢件和高强度板间的连接。
Low hydrogen electrode to be used for welding thick steel plate to casting and high tensile plates.
选择球墨铸铁的一个重要的原因在于球墨铸铁比铸钢成本低。
Select one of the major reasons cast iron ductile iron is lower than the cost of steel.
大型铸钢件在实际生产中易产生缩孔缩松、应力变形等缺陷。
Shrinkage and shrinkage porosity, stress and deformation often occurs during the production of heavy steel casting.
以材质划分为：碳钢、铸钢、合金钢、不锈钢、铜、铝合金等。
The material is divided into: carbon steel, cast steel, alloy steel, stainless steel, copper, aluminum alloy.
本文主要介绍了使用计算机模拟进行实际铸钢件工艺设计方法。
This paper focuses on the practical approach of rigging steel castings using computerized casting simulation.
KME在开发和生产连续铸钢用的铜模件方面树立起一座里程碑。
KME set milestones in the development and production of copper moulds for the continuous casting of steel.
研究表明，该铸钢节点在设计荷载的作用下，具有足够的强度和刚度；
The present investigation indicates that the cast steel joint subjected to its design loads has sufficient strength and rigidity.
衬板、搅拌叶片均采用高硬度、高韧性的耐磨合金铸钢，使用寿命长。
Lining board, mixing blades adopts high hardness and high toughness wear-resistant steel and long service life.
这是因为硅使贝氏体铸钢在高应力冲击磨损下表现出不同的失效机制。
The reason is that the impact wear mechanism is different for low and high Si bainitic cast steels.
介绍了湿型铸造中、小型铸钢件易产生的缺陷及防止缺陷所采取的工艺措施。
Defects in green casting process of small and middle steel_castings and the technical measures for protecting from defects are introduced.
用扫描电镜分析研究了铁基合金涂层对车轮铸钢材料抗热疲劳损伤机制的影响。
The mechanism of Fe-based alloy coating for thermal fatigue damage resistance of wheel cast steel was analyzed by SEM.
设计了一种中锰铸钢锤头材质，其在非强冲击条件下具有较好的加工硬化效果。
Designed a medium manganese cast steel used to making hammer, which has good work-hardness under non severe impact condition.
本文针对提高铸钢件冒口补缩效率问题，给出了微珠保温冒口的配方及生产工艺；
This article is written to explain how to improve the efficiency of riser feeding for cast steel items.
铸钢材质升级为低合金钢后，传统的砂型铸造工艺在生产中暴露出了一系列问题。
When low alloy steel replaced carbon steel castings, a series of questions were uncovered in traditional sand casting process.
悬浮浇注增加铸钢凝固期间的冷却强度，缩短凝固时间，增加体积凝固的倾向性。
In suspension pouring process the increase of cooling intensity during the solidification period will increase the tendency of volume solidification and decrease the solidification time.
因为球墨铸铁成本通常比铸钢低，而且强度更好，所以使用球墨铸铁更加经济实惠。
Because ductile iron usually costs less than CAST steel, yet offers comparable strength, it is more economical.
本文用具体数据资料论述采用空心微珠保温冒口给铸钢生产带来的技术-经济效益。
This paper by the real data shows that greater technical and economic benefit can be achieved with this technique in production of steel castings.
齿轮和齿轮托可以是铸铁或铸钢，可以有铸造或机加工的齿轮齿，取决于负载和应用环境。
The gears and gear brackets may be either cast iron or cast steel and may have cast or cut teeth, depending on the loads and the application.
本公司主要生产各种灰铁件、球铁件、铸钢件、高猛钢件等各种建筑、工程机械用零部件。
Our products: Various gray iron, ductile iron, common cast steel, low-alloy steel, high manganese steel, etc various parts of architectural and mechanical engineering.
本公司主要生产各种灰铁件、球铁件、铸钢件、高猛钢件等各种建筑、工程机械用零部件。
Our products: Various gray iron, ductile iron, common cast steel, low-alloy steel, high manganese steel, etc various parts of architectural and mechanical engineering.