并归纳出“不均匀混合区”和“不完全熔化区”的形貌特征。
The appearence characteristics of"heterogenous mixture zone'and'partially melted zone"are summed up.
其微观结构为典型的双模结构，由部分熔化区和完全熔化区组成；
The microstructure morphology of the coating deposited at moderated CPSP condition is typical bimodal microstructure which consists of partial melted region and full melted region.
裂纹扩展在焊缝区和半熔化区之间交替进行，并非严格按W／F界面破断。
Crack propagation conducts alternatively between the weld zone and the partially molten zone, and is not strictly to rupture at W/F boundary surface.
熔化区和固态相变区硬化相组织极为细小，马氏体呈微细针状，具有孪晶亚结构。
It is found that the structure of the hardened phase in melting and transformation zone is very tiny, the martensite appears to be tiny acicular and possesses twin substructure.
采用等效比热法来确定液相分数，假定固液相等同区来解决工件熔化区与非熔化区的移动边界。
Equivalent latent heat was adopted to determine liquid quantity and solid-liquid identity was adopted to solve moving interface between molten and solid region.
文中给出的算例表明，适当控制通入的电流强度，可以达到有效控制裂尖熔化区尺寸以及形成焊口的目的。
If a current with proper intensity has been switched on, the goal of controlling the melting and welding dimension effectively around the crack tip can be obtained.
注射工艺过程就是从给料斗送进粉状或粒状的塑料混合物，经过定量区和熔化区，然后将其注射到模具型腔中。
The process consists of feeding a plastic compound in powdered or granular form from a hopper through metering and melting stages and then injecting it into a mold.
结果表明，等离子表面冶金合金化涂层对基材具有良好的润湿性，基材表面熔化区的形成使得涂层与基材实现了完全的冶金结合。
Results indicated that plasma surface metallurgical coating of Fe-Cr-Ni-B-Si had well wettability, and metallurgical bonding was obtained between coating and substrate.
在爆炸焊接的过程中，结合区一薄层基体金属，在高温下将发生熔化、熔解或化合。
A thin layer of fusion zone is fused and compounded at the high tem" perature in explosion welding process."
焊接方法为脉冲熔化极混合气体保护焊，焊接板的中心裂纹处于焊缝与热影响区之间的熔合区。
The welding method used was a PC-GMAW process with mixture gases shielding. Central crack for the welded plate was located in the fusion zone between welding seam and heat-affected zone.
通过时大量熔化焊接头的金相观察，研究了熔化焊接头焊缝底部附近“不均匀混合区”的形貌特征。
The appearence characteristics of the heterogenous mixture zone near the bottom of weld metal in the fusion welded joint are studied through metallographic observations of many fusion welded joints.
通过时大量熔化焊接头的金相观察，研究了熔化焊接头焊缝底部附近“不均匀混合区”的形貌特征。
The appearence characteristics of the heterogenous mixture zone near the bottom of weld metal in the fusion welded joint are studied through metallographic observations of many fusion welded joints.