生产中一般控制芳香母粒质量分数5%左右。
The weight mass ratio of fragrant masterbatch should be controlled about 5%.
PET纤维中添加5%的抗菌母粒，纺丝正常。
PET fiber added with 5% antibacterial masterbatch yielded smooth spinning process.
本文介绍了高浓度珠光塑料母粒的性能、生产方法及应用前景。
An high concentrated pearlescent masterbatch was studied. Its properties, processing method and application were reviewed in this paper.
碳酸钙粉体是一种母粒，包含约85%碳酸钙基于聚烯烃树脂。
CACO3 masterbatch is a kind of masterbatch, contain about 85% Calcium Carbonate based on Polyolefin resin.
分析了母粒设计对纺前染色纤维的颜色和性能的影响的一些案例。
Some case studies showing the effect of master-batch design on color and properties of solution dyed fibers are examined.
用中心复合设计对离心式造粒机制备蔗糖小丸母粒的工艺作了优化。
The optimal conditions for preparing nonpareils by centrifugal granulator were investigated with central composite design.
论述了国内外LLDPE地膜着色专用碳黑母粒制造中的技术问题。
The key technical questions in producing carbon black masterbatch for coloring of LLDPE mulching film in China and abroad were reviewed.
分析了近年来发泡母粒的生产应用状况；展望了发泡母粒的应用动向。
It also analyzed the production and application of foaming master batch in recent years, and predicted the application trend of foaming master batch.
研究红磷阻燃母粒对玻纤增强尼龙66（PA66）阻燃性能的影响。
The effects of red phosphorus flame-retardant masterbatch on the flame-retardant properties of glass fiber reinforced PA66 were investigated.
试验说明，随着芳香母粒含量的增加，出现纺丝困难，纤维的断裂强度下降。
The spinning process became complicated and the fiber strength decreased with the addition of fragrant masterbatch.
用该母粒生产的流延膜，具有遮盖高、细度好、水份少、剥离强度大等特点。
The casting film produced with the masterbatch has the characteristics of high opacity, high fineness, low water content, large peeling strength and so on.
研究了不同填充母粒载体树脂对聚丙烯用母粒流动性及填料分散能力的影响；
The influence of several kinds of packed masterbatch carrier resins on the fluidity of polypropylene masterbatch and the dispersion of packed agent is investigated.
专用母粒： 双防母粒、抗静电母粒、抗菌母粒、高保温母粒、降温母粒等；
Masterbatch for: double-masterbatch, antistatic masterbatch, antibacterial masterbatch, masterbatch high insulation, cooling masterbatch;
经编防护网产品的生产流程包括母粒的制造、原料的准备、整经、编织和整理。
The production flow of warp knitted protective net includes manufacture of master batch, preparation of raw material, beaming, warp knitting and finishing.
研究了香料的选择、香母粒的制作、共混纺丝工艺及芳香聚丙烯的结构和性能。
The selection of spices, manufacture of spice matrix , technology of blending spinning, structures and properties of the fiber are discussed.
研究了作为黑母粒载体树脂的LDPE/LLDPE共混物对炭黑分散性的影响。
The effect of blends of LDPE/LLDPE as a carrier resin in black masterbatch, on the dispersion of carbon black was studied .
生产中母粒添加量为10%，纺丝温度和纺丝速度都低于常规纺时，可纺性良好。
When add amount of tourmaline masterbatch was 10 %, spin- ning temperature and speed were lower than conventional spinning method, the spinnability was good.
本文主要从工艺设定和生产控制的角度，对于母粒法生产全消光品种进行了探讨。
Thesis introduce the method which manufactured full dull PET by injecting master chip, by discussing the parameter chosen and control in process.
采用聚丙烯切片、抗菌母粒共混，制成高熔融指数的抗菌高速纺专用料进行纺丝。
With PP chips and antibacterial matrices blent, the antibacterial special raw material with high melt index is prepared for speed spinning.
本发明的磷氮类阻燃母粒适用于与其它塑料一起使用，并可有效提升阻燃剂的阻燃效果。
The phosphorus-nitrogen flame-retardant master batch can be used together with other plastics, and can effectively improve the flame-retardant effect of the flame retardant.
通过在聚酯切片中加入含金属氧化物母粒粉末，纺制了永久性防静电纤维，其电阻值为1。
A method is introduced, which mix polyester chip and metal-oxide powder, then spin staple fibre, the fibre has antistatic property as its resistance is 1.
以PE作为载体树脂，加入发泡剂AC、成核剂、包覆体制备出高性能PP用微孔发泡母粒。
Took PE as the carrier resin, joins foaming agent AC, nucleating agent and wrap agent, manufactured high performance foaming masterbatch which used for PP.
借助于dsc、X -射线衍射等测试手段，对聚丙烯母粒的热行为及结晶特性进行了分析。
By means of DSC and XRD, the thermal and crystalline properties of polypropylene masterbatch were instigated.
该抗菌抗紫外线复合功能健康纤维，使用复合功能健康纤维母粒，通过熔融高速挤压纺丝制得。
The antibacterial anti-ultraviolet compound function health fiber USES compound function health fiber master batches and is made through melting and extruding spinning in a high speed.
用共混法生产芳香纤维，简要介绍了芳香母粒的制备，芳香母粒的加入对纺丝及纤维性能的影响。
The preparation of fragrant fiber was introduced via blend spinning. The effect of the addition of fragrant masterbatch on the spinning situation and properties of the obtained fiber was discussed.
研究了炭黑母粒配方组成中分散剂、特制加工助剂以及炭黑母粒制备工艺等对炭黑最终分散性的影响。
The effect of dispersing agent, special processing agent in black masterbatch and processing technology of black masterbatch on the dispersion of carbon black was studied.
实验结果表明，聚烯烃阻燃母粒在生产阻燃聚烯烃制品中具有使用便利、阻燃效果和经济效益好等特点。
The lest results showed that the flame-retardant master had the characteristics as using conveniently, good effectiveness of flame retardance and good economic benefit in...
通过在纺丝过程中添加无机层状纳米银磷酸盐抗菌母粒制备出了一种持续、高效、广谱的抗菌锦纶6纤维。
A sort of permanent effective universal antibacterial polyamide 6 fibers have been prepared by adding layered nano-silver phosphate in spinning process.
通过在纺丝过程中添加无机层状纳米银磷酸盐抗菌母粒制备出了一种持续、高效、广谱的抗菌锦纶6纤维。
A sort of permanent effective universal antibacterial polyamide 6 fibers have been prepared by adding layered nano-silver phosphate in spinning process.