改善中心偏析关键在于控制液相穴末端的枝晶间液相的流动状况。
The control of the interdendritic flow at the end of the liquid pool is important to prevent the centreline segregation.
偏析的生成是因为局部加压使枝晶间的残余金属液产生局部流动而形成的。
Segregation is caused by remained metal liquid, which is driven by local pressure.
提出了预测铸钢件中缩松缺陷的数值方法，考虑了传热、枝晶间液相流动和气体析出等因素。
A numerical analysis method is presented to simulate the shrinkage porosity formation in steel castings on the basis of heat flow, interdendritic fluid flow and possible evolution of dissolved gases.
钎焊焊缝的枝晶间显微疏松导致的应力集中与微裂纹效应以及近焊缝区母材晶粒长大是导管早期疲劳开裂的主要原因。
The results show that the crack initiates at the outer surface of the weld comer and propagates into the steel base material with a high cycle fatigue mode.
钎焊焊缝的枝晶间显微疏松导致的应力集中与微裂纹效应以及近焊缝区母材晶粒长大是导管早期疲劳开裂的主要原因。
The results show that the crack initiates at the outer surface of the weld comer and propagates into the steel base material with a high cycle fatigue mode.