• 得出了完全再结晶温度开始过烧温度

    The fully recrystallization temperature and the on-set overheated temperature have also been obtained.

    youdao

  • 结果表明提高再结晶温度

    The results showed that the recrystallization temperature is increased by alloying chromium and molybdenum.

    youdao

  • 在工业加入微量提高结晶温度

    Trace lithium can improve recrystallization temperature of pure copper.

    youdao

  • 淬火组织经回火相变再结晶温度有所降低

    After tempering, structure inheritance reduces, the recrystallization temperature reduces.

    youdao

  • 结晶温度下,湮没特征表现连续回复过程

    At the reerystall temperature, the feature of annihilation appears as continual recovery process.

    youdao

  • 由于渗碳体阻碍晶粒长大,所以碳含量增加再结晶温度升高

    The cementite phase in steels increases the recrystallization temperature and abstracts the grain growth.

    youdao

  • 通过测量硬度观察组织,确定几种变形再结晶温度及其影响因素

    The recrystallization temperature of cold deformed steels and its influencing factors have been studied by measuring hardness values and structure observation.

    youdao

  • 再结晶温度以上材料内部缺陷损伤修复作用效果对塑性变形能力具有重要影响

    The effect of damage and fault healing has the great influence on the plasticity in materials over the recrystallization temperature.

    youdao

  • lc 4合金较低温度较高应变速率条件下,产生有效再结晶细化,而呈现一定的超塑性。

    The coarse crystalline LC4 alloy exhibit some superplasticity under lower temperature and higher strain rate, because it can create effective recrystallization refinement.

    youdao

  • 采用中断研究了取向硅钢结晶过程中的异常长大行为,确定二次再结晶发生温度范围

    The secondary recrystallization and its temperature range of grain oriented silicon steel have been studied by the method of interrupting secondary recrystallization annealing.

    youdao

  • 变形温度升高,复合材料发生动态回复结晶

    Dynamic recovery and recrystallization of the composite generate with the increasing of deformation temperature.

    youdao

  • lc 4合金较低温度较高应变速率条件下,产生有效结晶细化呈现一定超塑性

    Coarse crystalline LC4 Aluminium Alloy presents certain superplasticity at lower deformation temperature and higher strain rate because it can create effective recrystallize refinement.

    youdao

  • 结果表明,弯折压平交替变形,随热处理温度升高结晶增加

    The results show that after alternate deformation, with the increase of heat treatment temperature, the nucleation ratio of recrystallization rises.

    youdao

  • 随着变形温度降低、变形程度变形速率增大再结晶晶粒尺寸减小结晶体积分数增大。

    With the decreases of deformation temperature and increases of deformation degree and deformation rate, the recrystallized grain size decreases and the recrystallization volume percent increases.

    youdao

  • 结果表明:变形温度、变形速率变形程度流动应力再结晶晶粒尺寸均有不同程度影响

    The influences of deformation temperature, deformation rate and deformation degree on the flow stress and grain size are different. The deformation degree mainly influences the shape of flow curves.

    youdao

  • 相同速度下随着温度升高动态再结晶现象比较明显

    At the same velocity, the dynamic recrystallization phenomenon is rather distinct with the rise of temperature.

    youdao

  • 分辨电子显微镜观察到了催化剂合金中再结晶石墨形貌随温度、压力变化找到金刚石晶体形成的证据

    We have observed the change of recrystallized graphite morphology using a high-resolution electron microscope, and have found evidence of the diamond crystal-formation.

    youdao

  • 温度一定时,随着应变速率降低材料越容易发生动态结晶

    When the temperature is constant, the dynamic recrystallization was increased as the strain rate decreased.

    youdao

  • 但是如果温度过高产生结晶出现粗晶组织,还会导致性能的严重恶化。

    But if the annealing temperature is too high these will appear coarse-grained structure resulting from entire recrystallization.

    youdao

  • 动态再结晶晶粒尺寸随着变形温度升高而增大,随着应变速率升高减小

    The dynamically recrystallized grain size increases with increasing deformation temperature and reduces with increasing strain rate.

    youdao

  • 实验结果表明对于掺硅组分相同再结晶石墨,材料导电导热性能随着石墨化温度升高而增强力学性能却随之降低

    Experimental results showed that the thermal conductivity and electrical conductivity improved, but bending strength decreased with increasing graphitization temperature by the same amount of si.

    youdao

  • 研究结果表明金属材料确定后,热处理尺寸再结晶退火温度决定双金属环最终尺寸。

    The research result indicates that, when bimetal material is certain, the size of heat treatment mandrill and the temperature of re-crystallized anneal would decide the end size of bimetals wreaths.

    youdao

  • 处理温度高低不仅影响第二基体中的溶解程度影响合金回复结晶过程进行的程度

    The temperature of solid solution treatment affected not only the degree of the second phase dissolved in the matrix alloy, but also the recovery and recrystallization processing level of the alloy.

    youdao

  • 提高温度可以促进热轧再结晶增加成品有利织构组分降低提高感。

    High finish rolling temperature promotes the recrystallization of hot-rolled strip, increases favorable texture components, decreases the core loss, and increases magnetic induction of final product.

    youdao

  • 结果表明氏体的再结晶发生钢的正常淬火温度以上温度范围,并在该范围内存在晶粒细化效果最佳温度区域;

    The results showed that the austenite recrystallization occurs in a temperature range biger than thenormal quenching temperature and there is an optimum temperature range for the grain refining.

    youdao

  • 通过回归分析建立了动态再结晶晶粒尺寸温度应变速率之间定量关系

    The quantitative relationship between the recrystallized grain size and the temperature as to as the strain rate is established by the regression analysis.

    youdao

  • 研究了工业纯铜T277K温度下快速压缩变形组织变化结晶退火温度、时间对其组织、性能影响。

    The microstructure and hardness of T2 copper subjected to stamping deformation at 77 K and subsequently recrystallization annealing were studied.

    youdao

  • 或使瓶颈结晶(),结晶瓶颈能耐温度

    Alternatively, the bottle neck is crystallized (and turns white). Crystallized PET bottle neck could stand up to a high hot fill temperature.

    youdao

  • 变形量,变形温度,变形速度,变形间歇时间等因素再结晶晶粒长大重要影响

    Deformation, deformation temperature, deformation velocity and breaks after deformation have important influence on recrystallization grains grown.

    youdao

  • 变形量,变形温度,变形速度,变形间歇时间等因素再结晶晶粒长大重要影响

    Deformation, deformation temperature, deformation velocity and breaks after deformation have important influence on recrystallization grains grown.