钢和铸铁都有共析、亚共析和过共析这三种组织。
Both steel iron and cast iron have the structures of eutectoid, hypoeutectoid and hypereutectoid.
含碳量少于共析体(低于0.77%)的钢称为亚共析钢。
Steels having less than the eutectoid amount of carbon (less than 0.77%) are known as hypo-eutectoid steels.
含碳量少于共析体(低于0.77%)的钢称为亚共析钢。
Steels shaving less than the eutectoid amount of carbon (less than 0.77%) are known as hypo-eutectoid steels.
硼有加速珠光体成长率的作用,无论在亚共析或共析钢中皆有同样的现象产生。
It was found by experiments thatboron increased the growth rate of pearlite, both in hypoeutectoid and eutectoid steels.
研究了两种基体的亚共析钢经激光处理后,其硬化层的硬度梯度及其磨损特性。
The hardening gradient and the character of abrasion in hardening layer of hypoeutectoid steel with two kinds of matrixes that was treated by laser beam have been studied.
本文是针对塑压模的热处理变形控制的研究。特别是对亚共析钢制塑压模更为有效。
This paper mainly researches on the control of heat treatment deformation of plasticpressing mould, the method is especially effective to the mould made of hyposteel.
当这种钢冷却时,就像图2.1的z - z线所示,除了初步的或预共析状态用渗碳体取代铁素体外,其余类似亚共析钢的情况。
When such steel cools, as shown in zz 'of Fig. 2.1 the process is similar to the hypo-eutectoid case, except that the primary or pro-eutectoid phase is now cementite instead of ferrite.
结果表明,对于亚共析钢,在中温区变形、保温后可使先共析铁素体和珠光体组织大大细化,显著改善钢中铁素体和珠光体的分布状况;
The results show that, in hypoeutectoid steels, deformation at medium temperature may fine the structure and improve the distribution of ferrite and pearlite greatly;
结果表明,对于亚共析钢,在中温区变形、保温后可使先共析铁素体和珠光体组织大大细化,显著改善钢中铁素体和珠光体的分布状况;
The results show that, in hypoeutectoid steels, deformation at medium temperature may fine the structure and improve the distribution of ferrite and pearlite greatly;