This paper summed up the tensile strength of steel wire, annealing temperature and annealing time by experimental datas of wire annealing.
利用钢丝退火试验数据，总结了钢丝的抗拉强度、退火温度和退火时间的关系。
Company in early 2007 the focus of research induction annealing tinning machine, power-saving rate and old-fashioned electric wire annealing machine compared to up to 70%.
公司于2007年初重点攻关感应式退火镀锡机，节电率和老式电热丝退火机相比最高达70%。
Through various drawing methods and annealing steps, We produces different physical characteristics in wire of a given size.
通过各种绘图方法和退火步骤，我们产生不同的物理特性，在一个给定大小的丝。
Because after annealing line is very soft, corresponding to different wire diameter to use appropriate tension weight, if wire diameter small tension is big, will be the wire diameter and thin.
因为退火后的线已经很软了，对应不同的的线径要采用合适的张力重量，如果线径小张力大，就会把线径拉细了。
But in the continuous annealing, copper wire heating make wire become soft, line itself has certain extension.
但是在连续退火时，铜线发热使线材变软，线本身就有一定的延伸。
Triangular structure of the outer conductive copper wheel points inside and outside two groove, the copper wire inside groove introduced, complete annealing.
三角结构的外层导电铜轮分内外两沟，铜线经内沟引入，完成退火。
Taiwan to introduce advanced technology manufacturing hydrogen retired oven, stainless steel wire is conducive to improve the annealing of light brightness, improve yield and quality.
引进台湾先进技术生产制造的氢退炉，有利于提高不锈钢丝退火的光亮度，产量与质量的提高。
Base on experiment, this article presented some optimum technological parameters of middle annealing that can stabilize the processing properties of molybdenum wire.
本文在实验的基础上提出的适合中间退火的工艺可稳定钼丝加工性能。
Through doing some technical remakes on well resistance furnace the annealing quality of steel wire has been improved and the energy consumption has been cut down.
井式电阻炉经技术改造后提高了钢丝的退火质量，降低了能耗。
We meet the needs of many diverse industries through our specialized methods of processing wire including: Cladding, Drawing, Annealing, Electroplating, Flat Wire Rolling and Hot Solder Dipping.
本公司拥有专业的线材处理技术，如包层、拉制、退火、电镀、扁平线绕圈和热浸焊等，能够满足多种工业领域的特殊要求。
To give technical transformation measures of heat-treatment furnace in general use, directed to the problems in wire coils annealing.
针对钢丝盘卷料退火存在的问题，对常用热处理炉提出技术改造措施；
The influences of two different kinds of annealing processes on properties of Ni-Al composite wire were presented.
分析了两种不同的退火工艺对镍铝复合丝性能的影响。
Copper wire color (dark red or white) : continuous annealing in the work period of the line burn soft and pass cooling section after cooling can achieve lead not hot, without water.
铜线变色(暗红或发白)：连续退火在工作段把线烧软，还要经过冷却段冷却后才能达到引出线不烫、不带水。
The company was founded in 1996, is a manufacturer of wire drawing machine, annealing tinning machine, wire machine, extrusion machines and other electrical equipment, specialized production factory.
公司创建于1996年，是一家生产拉丝机、退火镀锡机、绞线机、押出机等多种电工设备的专业生产厂家。
The max. annealing current is up to 2500A, which ensures that the elongation of annealed wire can reach 30%.
最大退火电流高达2500A，保证了线材经退火后的延伸 率高达30%。
Its main purpose is for annealing and winding of stainless steel wire, copper wire and other metal wires, and the uniform moment wire-rewinding assembly may used in combination or in single.
其主要用途为不锈钢丝、铜丝及其它金属丝线的退火、绕线，匀速力矩收线机总成既可组合使用，也可单体使用。
The article elaborated the remake measures and contrasted the annealing quality of steel wire after remake to that before remake.
文中详述了改造措施，对比了改造前后钢丝的退火质量。
As the annealing temperature rises, the resistivity of alloyed wire reduced and thermal potential raised.
随退火温度升高，合金丝电阻率下降，热电势升高。
ER110S, a kind of low-carbon steel welding wire alloy, which is processed by a traditional annealing, is often broken for the work-hardening in the follow-up drawing process.
传统工艺退火处理后的合金低碳钢焊丝ER110S，在后续的拉拔加工中，加工硬化导致经常断丝；
The causes for the initiation of the "spark phenomenon" during continuous wire drawing and annealing are traced. Simple measures to extinguish the spark are proposed.
本文对连续拉丝过程中出现铜线表面“打火现象”的原因进行分析，并提出简单的消除方法。
If the red hot wire directly out of the cooling, the annealing is not complete, steel wire hardness, not easy to spring.
如果把烧红的钢丝直接取出冷却，则退火不完全，钢丝硬度大，不易绕制弹簧。
Purpose : heat treatment of general metals, aluminum alloy, spheroidizing wire and bright annealing copper wire.
用途：一般线材处理，铝合金线材，球状化线材，光亮铜线等。
Applictions: heat treatment of general metals, aluminum alloy, spheroidizing wire and bright annealing copper wire.
用途：一般线材处理，铝合金线材，球状化线材，光亮铜线等。
Applictons: heat treatment of general metals, aluminum alloy, spheroidizing wire and bright annealing copper wire.
用途：一般线材处理，铝合金线材，球化线材，光亮铜线等。
The best general working rate that Nb-1Zr wire was recrystallized completely was about 82% at a given annealing temperature.
试验结果表明，在一定的温度下，铌锆合金丝材达到完全再结晶的最佳总加工率在82%附近。
The best general working rate that Nb-1Zr wire was recrystallized completely was about 82% at a given annealing temperature.
试验结果表明，在一定的温度下，铌锆合金丝材达到完全再结晶的最佳总加工率在82%附近。
应用推荐