The influence of Lanthanum, Cerium, Yttrium, Praseodymium and Neodymium on weld hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron was studied.
研究了纯镍铸铁焊条冷焊时，稀土金属镧、铈、镨、钇及钕对焊缝热裂纹敏感性的影响规律，并分析了铈对焊接接头力学性能和加工性能的影响。
The front impact roller causes transverse plastic compression strain in the weld which is in the brittle temperature range, which counteracts the tensile strain which leads to hot cracking.
前轮对处于脆性温度区间的焊缝金属施加一个横向挤压塑性应变，减小甚至抵消致裂的拉伸应变，防止了焊接热裂纹的产生。
Weld with trailing impactive rolling (WTIR) is a new technique to reduce the residual stress and distortion and prevent hot cracking of thin-walled structure.
随焊冲击碾压是一种控制薄壁结构焊接应力变形、防止热裂纹的新方法。
The improvement of microstructure leads to a considerable reduction of the susceptibility of hot cracking of weld metal as indicated by the transverse-varestraint test.
增加焊缝中的共晶数量并改善其分布形态，从而有助于降低焊缝金属的热裂纹敏感性。
Neodymium can increase weld metal hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron.
纯镍铸铁焊条中加入稀土钕会增加焊缝热裂敏感性。
Neodymium can increase weld metal hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron.
纯镍铸铁焊条中加入稀土钕会增加焊缝热裂敏感性。