It is indicated that the wear coefficient decreases with the decrease of the scaling and the wear becomes serious with the increase of the applied loading or the rotation Numbers.
仿真结果表明，尺度减小，磨损系数变小，增大载荷或增加微枢轴旋转次数均会加剧磨损程度。
With graphite particle content increasing from 5% to 20%, wear weight-loss and friction coefficient of the composites are obviously declined, greatly improving wear resistance of the composites.
随着石墨颗粒含量从5%增加到20%，镁合金基复合材料的耐磨性得到明显的改善，磨损质量损失与摩擦系数都降低到较低水平。
Low friction-the coefficient of friction between the chip and tool should be low. This would allow for lower wear rates and better chip flow.
低摩擦系数—切屑与刀具间的摩擦系数应当较低。这会使磨损率较小及切屑流动更好。
The properties of coatings. e. g. tensile strength, expansion coefficient, wear volume under given conditions and porosity, etc. were tested.
测定了涂层抗拉强度、膨胀系数、一定条件下的磨损体积、气孔率等性能。
This surface has extreme hardness (60 RC. ), excellent wear and corrosion resistance, and low coefficient of friction.
这表面有极高的硬度（60局。），耐磨性和耐腐蚀性，低摩擦系数。
However, in some application conditions, low hardness, big friction coefficient and poor wear resistance confine its extensive application in engineering.
然而，在某些应用条件下，钛合金的硬度低，摩擦系数大，耐磨性差。
The effects of metal base content and NiCr alloy addition on hardness, friction coefficient and wear rate of the composites were studied.
研究了金属基体及其中镍铬合金的含量对复合材料的硬度、摩擦系数和磨损率的影响。
The tube surface has extreme hardness (60 RC.), excellent wear and corrosion resistance, and low coefficient of friction.
管表面有极大的硬度(60钢筋混凝土。)，良好的耐磨性和耐腐蚀性，低摩擦系数。
If grit is sharp anp irregular, the coefficient of friction, consumption of energy and wear speed will be greater.
尖锐的、不规则形状的磨粒，摩擦系数、能量消耗、磨损速度都较大。
The results show that the friction coefficient and wear rate decrease with the increase of the graphite content.
研究表明，随著石墨含量的增加，摩擦系数和磨损量减小。
Titanium nitride coating has great application in industry owing to its superior properties, such as good wear and corrosion resistance, low friction coefficient and good thermal barrier properties.
氮化钛涂层因具有良好的耐蚀性、耐磨性及低的摩擦系数在工业上得到广泛应用。
Under a wide range of P and V value, there are very low friction coefficient and wear, high dimensional stability for coating-metal pairs and no any damage during the test of nylon coating.
涂层在较大的P、V值范围内与各类配副均具有极低的摩擦系数和磨损量以及很高的尺寸稳定性；长期工作过程中，涂层未出现任何破坏现象。
The effect of load on the friction coefficient becomes small during the steady stage of wear.
磨损达到稳态后载荷对复合材料摩擦系数的影响不大。
It has the best chemical corrosion resistance among known plastics. Without being aging, lowest friction coefficient, wear resistance.
在已知的塑料中，四氟具有最好的耐腐蚀性，不老化，油封低磨擦系数，耐磨擦。
The friction coefficient of amphiphobic surface in seawater is smaller than that in water while the wear loss of the former is bigger.
双疏表面在油介质中的摩擦系数和磨损量最小，在海水中的摩擦系数小于水，磨损量大于水。
The comparison of the results of P01 and P02 showed that P01 had slightly lower coefficient of friction, but its wear was larger, indicating its larger humidity sensitivity.
比较P01和P02的结果发现，虽然P 01试样的摩擦系数总体稍低，但磨损量较大，显示了P 01对湿度的敏感性稍大。
Laser cladding on titanium alloys can improve the surface properties, obtain the coatings with high hardness, good wear resistance and low friction coefficient.
在钛合金表面进行激光熔覆，可提高钛合金的表面性能，获得高硬度、耐磨性能好、低摩擦系数的熔覆层。
The friction coefficient and wear rate decreased with increasing lead content, especially the anti seizure property of al Pb alloys containing 20wt. % and 25wt. % lead was improved remarkably.
随着铅含量增加，合金的摩擦系数与磨损率显著下降，尤其铅含量为2 0 %与2 5 %的合金抗咬合性能明显提高。
Although the specific wear rates of the coatings increase obviously as the annealed temperature increase, the coefficient of friction exhibits decrease first and then increase.
随退火温度的升高镀层摩擦系数呈现出先降低后升高的变化趋势，比磨损率逐渐增大。
Ta ion implantation reduces the friction coefficient and friction and wear volumes of the Al bronze. Therefore, Ta ion implantation can improve wear resistance of Al bronze.
铝青铜的摩擦系数显著降低，单位时间内磨损质量损失显著减小，因此明显提高了铝青铜的耐磨性能。
Test results show that the developed brake composites have fairly stable friction coefficient, good fading resistance, low wear rate and...
对比试验表明，所研制的制动材料摩擦系数稳定，抗衰退性能好，磨损率较小，具有较大的性能价格比优势。
It shows that the elastic modulus and the molecular component of friction coefficient of the pulley material have great influence on the wear resistance of wire rope.
结果表明，绳轮材料的弹性模量和摩擦系数分子分量，对钢丝绳耐磨性能有很大影响。
Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical properties.
低摩擦系数非常低，否则给予机械性能不变的磨损。
Results show that the addition of PTFE can not only increase the wear resistance of PC, but also decrease its friction coefficient.
结果表明，PTFE的添加不仅可以提高PC的耐磨性，而且还可降低其摩擦系数；
Experimental results show that POB reduces the friction coefficient and increases the wear resistance of PTFE.
结果表明，添加pob降低了PTFE的摩擦系数，提高了PTFE的耐磨性。
The friction coefficient and wear resistance of compacted graphite cast iron brake shoes with phosphorous are systematically investigated in this paper.
本文对含磷蠕墨铸铁闸瓦的摩擦系数与耐磨性进行了系统的研究。
Coefficient of wear ability "is introduced to show the wear ability of cemented carbide coated with diamond film."
为表征金刚石薄膜涂层硬质合金的耐磨性能，引入了“耐磨系数”指标。
Z6, Semi-ceramic with low asbestos fibers. High friction coefficient, high temperature tolerance and less wear ratio.
半陶瓷低石棉型，特点：高温热稳定性好，刹车舒适，无噪音，摩擦系数稳定，耐磨性好， 米黄色。
The ha coating deposited by biomimetic method has lower friction coefficient and better wear resistance compared with the composite coatings.
而与两种复合涂层相比，仿生沉积HA涂层有较低的摩擦系数和更好的耐磨性能。
The ha coating deposited by biomimetic method has lower friction coefficient and better wear resistance compared with the composite coatings.
而与两种复合涂层相比，仿生沉积HA涂层有较低的摩擦系数和更好的耐磨性能。