Transgranular cleavage fracture is shown for the charged layer in tensile specimen.
拉伸试样表面充氢层的断口是穿晶解理断口。
The increase in ductility can be attributed to the increase in ratio of transgranular fracture.
穿晶断裂比例的增加是延性提高的原因。
The indentation cracks propagation is typified by an intergranular and transgranular mixed mode.
压痕裂纹扩展为沿晶和穿晶混合模式。
Transgranular fracture. Fracture of polycrystalline materials by crack propagation through the grains.
多晶材料裂纹穿过晶粒扩展而断裂。
The results showed that it was chlorine ion that resulted in transgranular stress corrosion cracking in brass tubes.
结果表明，黄铜管的开裂为氯离子引起的穿晶应力腐蚀开裂；
Once initiated, cracks would propagate perpendicularly to the loading direction and the specimens exhibited transgranular fracture.
裂纹形成后垂直于加载轴方向扩展，试样呈穿晶断裂。
And the low-temperature fracture was mainly quasicleavage step, this demonstrated that the fracture mede was transgranular type fracture.
低温拉伸时呈穿晶断裂，断口主要为准解理台阶；
However, at the higher temperatures, transgranular cracking and coupling of intergranular and transgranular thermal cracking are the main cracking for Beishan granite.
在较高温度时，热开裂以穿颗粒热开裂及沿颗粒穿颗粒混合热开裂为主。
Micro characteristic of cracks propagation research: the path of crack propagation in the heat-affected zone and weld metal is the mix of transgranular and intergranular.
裂纹扩展的微观特征研究：在热影响区与焊缝区的裂纹扩展均为沿晶与穿晶混合型。
To date, two forms of SCC penetration from the external surface of the pipeline have been recognized: one is the intergranular SCC, the other is a kind of transgranular SCC.
到目前为止，有两种形式的从管道的外表面的SCC渗透已确认：一种是晶间scc中，另一种是一种穿晶scc。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
研究表明该钢具有较好的抗应力腐蚀性能，其应力腐蚀断裂形貌为穿晶、解理断裂，并有二次裂纹。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
研究表明该钢具有较好的抗应力腐蚀性能，其应力腐蚀断裂形貌为穿晶、解理断裂，并有二次裂纹。